002.0_Attachment 1-A_Sherwin-Williams Marine Coatings.pdf

STATE OF MARYLAND – DEPARTMENT OF NATURAL RESROUCES – MARINE OPERATIONS – DECK BARGES

BARGES (3) : CAMBRIDGE, CHESAPEAKE & BALTIMORE (80’ X 26’ X 5’)

HAUL OUT PERIOD – TBD

YARD: TBD

ATTENTION: MIKE SIMONSEN

SPECIFICATION WRITTEN BY: DAVID NORWICZ – MARINE COATINGS REPRESENTATIVE – SHERWIN WILLIAMS MARINE DIVISION

SHERWIN-WILLIAMS MARINE COATINGS “QUICK” SPECIFICATION AND MATERIAL ESTIMATE

STEEL HULL SPECIFICATION:

ITEMS TO INCLUDE: UNDERWATER HULL, SIDE-SHELL, BUOYANCY CHAMBERS AND DECK SURFACES

100% PRESERVATION OF THE BARGE TO INCLUDE A FULL SSPC-SP6 COMMERCIAL BLAST OR SSPC-SP12 / NACE 5 WJ-2

UNDERWATER HULL (KEEL TO WL ~ 2.5’) ~2,610 ft2

SURFACE PREPARATION: *SSPC-SP1 SOLVENT CLEANING: POWER WASH UPON ARRIVAL WITH NO LESS THAN 5000 PSI AND WATER BLASTER TO REMOVE

FOULING AND LOOSELY ADHERED COATINGS. PERFORM A FULL SSPC-SP6 COMMERCIAL BLAST OR SSPC-SP12 - UHP WJ-2 BLAST PRIOR TO COATING. FLASH RUST

LEVEL (M) MODERATE IS ACCEPTABLE.

PRODUCT DESCRIPTION

VOLUME

SOLIDS

COAT

SEQUENCE

COLOR WFT RANGE DFT RANGE

PRACTICAL

COVERAGE

RECOAT

MINIMUM

RECOAT

MAXIMUM

REDUCER

SEAGUARD 5000 73% +- 2% FULL GRAY 7.0 – 10.0 5.0 – 7.0 164 ft2 - 117 ft2 6 HOURS 90 DAYS R7K130

SEAGUARD TIE COAT 67% +- 2% FULL YELLOW 7.0 – 10.0 5.0 – 7.0 164 ft2 - 117 ft2 5 HOURS 3 DAYS MEK

SEAGUARD ABLATIVE AF 65% +- 2% FULL RED 4.0 – 7.0 2.5 – 4.0 292 ft2 - 183 ft2 4 HOURS UNLIMITED VM&P

SEAGUARD ABLATIVE AF 65% +- 2% FULL BLACK 4.0 – 7.0 2.5 – 4.0 292 ft2 - 183 ft2 4 HOURS UNLIMITED VM&P

NOTES: The Antifoulant coat shall be applied when the Intermediate SeaGuard TIE-COAT is DRY TO TOUCH. Recoat window not to exceed 4 days

FREEBOARD (SIDE-SHELL TO DECK EDGE) ~ 530 ft2

SURFACE PREPARATION: *SSPC-SP1 SOLVENT CLEANING: POWER WASH UPON ARRIVAL WITH NO LESS THAN 5000 PSI AND WATER BLASTER TO REMOVE

FOULING AND LOOSELY ADHERED COATINGS. PERFORM A FULL SSPC-SP6 COMMERCIAL BLAST OR SSPC-SP12 - UHP WJ-2 BLAST PRIOR TO COATING. FLASH RUST

% VOLUME

SOLIDS

COAT

SEQUENCE

COLOR WFT RANGE DFT RANGE

PRACTICAL

COVERAGE

RECOAT

MINIMUM

RECOAT

MAXIMUM

REDUCER

SEAGUARD 5000 73% +- 2% FULL RED 7.0 – 10.0 5.0 – 7.0 164 ft2 - 117 ft2 6 HOURS 90 DAYS R7K130

SEAGUARD 5000 73% +- 2% FULL GRAY 7.0 – 10.0 5.0 – 7.0 164 ft2 - 117 ft2 6 HOURS 90 DAYS R7K130

SHERLOXANE 800 GLOSS 90%+-2% FULL 26373 5.0 - 7.0 4.0 - 6.0 250 ft2 -- 175 ft2 3 HOURS 1 YEAR MEK

FREEBOARD NOTES:

1.) DRAFT MARKINGS / BARGE IDENTIFICATION– OVERCOAT SPECIFIED FREEBOARD SYSTEM WITH 1-2 COATS OF WHITE SHERLOXANE 800 GLOSS WHITE.

2.) FREEBOARD COLOR TO BE CONFIRMED BY DNR.

MAIN DECK ~ 2,080 ft2

SURFACE PREPARATION: *SSPC-SP1 SOLVENT CLEANING: POWER WASH UPON ARRIVAL WITH NO LESS THAN 5000 PSI AND WATER BLASTER TO REMOVE

FOULING AND LOOSELY ADHERED COATINGS. PERFORM A FULL SSPC-SP6 COMMERCIAL BLAST OR SSPC-SP12 - UHP WJ-2 BLAST PRIOR TO COATING. FLASH RUST

SOLIDS

COAT

SEQUENCE

COLOR WFT RANGE DFT RANGE

PRACTICAL

COVERAGE

RECOAT

MINIMUM

RECOAT

MAXIMUM

REDUCER

SEAGUARD 5000 73% +- 2% FULL RED 7.0 – 10.0 5.0 – 7.0 164 ft2 - 117 ft2 6 HOURS 90 DAYS R7K130

SHERLOXANE 800 GLOSS 90%+-2% FULL 26373 5.0 - 7.0 4.0 - 6.0 250 ft2 -- 175 ft2 3 HOURS 1 YEAR MEK

NOTES: BROADCAST 36 MESH ALUMINUM OXIDE INTO WET FILM OF SEAGUARD 5000 GRAY. SWEEP EXCESS PRIOR TO APPLICATION OF SHERLOXANE 800

DECK COLOR TO BE FEDERAL STANDARD 26373 LIGHT GRAY TO BE CONFIRMED BY DNR

BUOYANCY CHAMBERS ~ 5,720 ft2

SURFACE PREPARATION: *SSPC-SP1 SOLVENT CLEANING: POWER WASH UPON ARRIVAL WITH NO LESS THAN 5000 PSI AND WATER BLASTER TO REMOVE

FOULING AND LOOSELY ADHERED COATINGS. PERFORM A FULL SSPC-SP6 COMMERCIAL BLAST OR SSPC-SP12 - UHP WJ-2 BLAST PRIOR TO COATING. FLASH RUST

SOLIDS

COAT

SEQUENCE

COLOR WFT RANGE DFT RANGE

PRACTICAL

COVERAGE

RECOAT

MINIMUM

RECOAT

MAXIMUM

REDUCER

SEAGUARD 5000 73% +- 2% FULL WHITE 7.0 – 10.0 5.0 – 7.0 164 ft2 - 117 ft2 6 HOURS 90 DAYS R7K130

NOTES: SCOPE OF PREPARATION TO BE CONFIRMED AT TIME OF DRY-DOCKING AFTER AN INSPECTION OF THE CHAMBERS HAS BEEN COMPLETED

*** BARGE CAMBRIDGE & BALTIMORE ONLY 30” WAIST COLLAR ~ 400 ft2***

SURFACE PREPARATION: *SSPC-SP1 SOLVENT CLEANING: POWER WASH UPON ARRIVAL WITH NO LESS THAN 5000 PSI AND WATER BLASTER TO REMOVE

FOULING AND LOOSELY ADHERED COATINGS. PERFORM A FULL SSPC-SP6 COMMERCIAL BLAST OR SSPC-SP12 - UHP WJ-2 BLAST PRIOR TO COATING. FLASH RUST

SOLIDS

COAT

SEQUENCE

COLOR WFT RANGE DFT RANGE

PRACTICAL

COVERAGE

RECOAT

MINIMUM

RECOAT

MAXIMUM

REDUCER

SEAGUARD 5000 73% +- 2% FULL RED 7.0 – 10.0 5.0 – 7.0 164 ft2 - 117 ft2 6 HOURS 90 DAYS R7K130

SHERLOXANE 800 GLOSS 90%+-2% FULL 26373 5.0 - 7.0 4.0 - 6.0 250 ft2 -- 175 ft2 3 HOURS 1 YEAR MEK

NOTES: 30” WAIST COLLAR ONLY ON BARGE CAMBRIDGE & BALTIMORE. BARGE CHESAPEAKE DOES NOT HAVE A WAIST COLLAR INSTALLED.

WAIST COLLAR COLOR TO BE CONFIRMED BY DNR

** END OF SPECIFICATION **

➢ SCOPE OF WORK SHALL BE REVIEWED AT TIME OF DOCKING

➢ A DRY DOCK REPORT WILL BE COMPLETED AND PRESENTED UPON COMPLETION

➢ ALL EXCESS MATERIAL WILL BE PICKED UP AND RETURNED FOR CREDIT OR COUNTED AND LEFT FOR NEXT PROJECT. EXCESS MATERIAL MUST BE IN

CLEAN, UN-OPENED CONTAINERS.

➢ ANY CHANGES TO THIS SPECIFICATION WILL BE DONE SO IN WRITING IN A TIMELY MANNER AND WILL BE PRESENTED TO ALL PARTIES INVOLVED IN

THE COATINGS PROJECT.

➢ IF OPTIONS ARE INCLUDED IN THE SCOPE OF WORK PLEASE ADVISE SW SO WE CAN PLAN FOR MATERIALS.

PROJECT NOTES:

1) THIS SPECIFICATION OUTLINES THE MINIMUM REQUIREMENTS FOR SURFACE PREPARATION, APPLICATION, AND INSPECTION OF PROTECTIVE COATINGS FOR CORROSION

CONTROL.

2) THE SHIPYARD SHALL CONDUCT A PRE-JOB CONFERENCE TO REVIEW AND CLARIFY THE SPECIFICATION – INCLUDING SURFACE PREPARATION, APPLICATION PROCEDURES, AND ANY SPECIAL CONDITIONS THAT MAY BE REQUIRED. THE CONFERENCE SHALL INCLUDE REPRESENTATION FROM VESSEL OWNER, THE BUILDER’S AND/OR THE PAINT

CONTRACTOR’S REPRESENTATIVE, AND SHERWIN-WILLIAMS.

3) SURFACE PREPARATION AND COATING APPLICATION WILL BE SUBJECT TO INSPECTION BY VESSEL OWNER OR THEIR DESIGNATED INSPECTOR AT ALL TIMES.

4) THE PAINT MANUFACTURER’S PRODUCT DATA SHEETS AND SPECIFICATIONS FOR MIXING, REDUCTION, APPLICATION AND CURING SHALL BE FOLLOWED. ANY DEVIATION

REQUEST FROM THE DATA SHEET REQUIREMENTS MUST BE SUBMITTED IN WRITING AND WILL BE REVIEWED BY SHERWIN-WILLIAMS AND VESSEL OWNER.

5) A “STRIPE” COAT TO BE APPLIED ONTO WELD SEAMS, EDGES OF PLATING, SCALLOPS, DRAIN HOLES AND ANY OTHER AREAS HAVING SHARP EDGES.

6) THE PAINTING OF THE EXPOSED STRUCTURAL STEEL SURFACE SUCH AS OUTSIDES OF SHELL, DECKHOUSE, FUNNEL, STACKS, HANDRAILS, ETC., AND OF ALL LIVING SPACE AND

PASSAGES IN LIVING QUARTERS TO BE FREE FROM SAGS, DRIPS, OVERSPRAY AND RUNS.

7) SPECIFIED PAINT THICKNESS IS TO BE CONSIDERED AS MINIMUM THICKNESS IN DRY CONDITION. THE DRY FILM THICKNESS TO BE MEASURED AFTER EACH COAT TO

CONFIRM ADEQUATE THICKNESS. UNDER WATER HULL PAINT THICKNESS TO BE CHECKED BEFORE AND AFTER APPLICATION OF ANTI-FOULING PAINT AND RECORDED.

FOLLOW SSPC-PA 2 PROCEDURE FOR MEASUREMENT OF DFT.

8) ALL WELDS IN THE UNDERWATER HULL, FREEBOARD, SUPERSTRUCTURE, DECKS, AND ALL TANKS SHALL BE PREPARED TO NACE STANDARD SP 0178 GRADE D.

9) WELD PREPARATION FOR ALL INTERIOR DRY VOIDS AND SPACES MUST RECEIVE MINIMUM REQUIRED SURFACE PREPARATION SSPC-SP2 “HAND TOOL CLEANING” OR SSPC-

SP3 “POWER TOOL CLEANING”.

10) ALL WELD DYE PENETRANT (DP) MUST BE REMOVED PRIOR TO APPLICATION.

11) AREAS OF DAMAGE AFTER APPLICATION MUST RECEIVE MINIMUM REQUIRED SURFACE PREPARATION SSPC-SP2 “HAND TOOL CLEANING” OR SSPC-SP3 “POWER TOOL

CLEANING”.

REPAIR PROCEDURES:

REPAIR OF DAMAGED AREAS: ALL SURFACES WHERE COATING IS DAMAGED DURING FABRICATION, TRANSPORTATION AND ERECTION SHALL BE REPAIRED AS FOLLOWS:

1) TOP-COAT DAMAGED BUT BASE COAT UNDAMAGED: REPAIR BY REMOVING DAMAGED COATING WITH SANDPAPER OR OTHER MEANS ACCEPTABLE TO VESSEL OWNER.

FEATHER EDGES OF ADJACENT PAINTED SURFACES 1” – 2” AND APPLY TOP-COAT AS SPECIFIED FOR DAMAGED AREA LOCATION.

2) COATING DAMAGED TO BARE METAL: REPAIR BY BLASTING DAMAGED AREA TO NEAR WHITE METAL SSPC-SP10 / NACE 2 OR CLEAN PER SSPC-SP 11, FEATHER ADJOINING

PAINT SURFACES WITH SANDPAPER AND PROVIDE A SMOOTH TRANSITION AND APPLY THE SPECIFIED COATING SYSTEM FOR DAMAGED AREA LOCATION

MISSED RECOAT WINDOW:

1) IF THE RECOAT WINDOW IS EXCEEDED, THE AREA TO BE RECOATED WILL MUST BE THOROUGHLY ABRADED. PRIOR TO PROFILING, ALL SURFACES SHALL BE CLEANED PER

SSPC-SP1. ABRADE WITH 80 GRIT SANDPAPER, ABRASIVE BLASTING, OR EQUIVALENT.

2) IF ABRASIVE BLASTING IS SELECTED: DRY OR WET ABRASIVE BLASTING SHOULD BE DONE IN A MANNER SIMILAR TO “SWEEP BLASTING” WITH A FINE TO MEDIUM GRIT

MEDIA.

3) THE SURFACES SHOULD BE EVENLY BLASTED TO CREATE A PROFILED SURFACE.

COLOR SELECTION:

PAINTING AND COLOR CODING FOR SAFETY, IDENTIFICATION AND LOGO PURPOSES SHALL BE DONE IN ACCORDANCE WITH OWNER’S STANDARD COLORING SCHEME

SHOP NOTES / QA:

1) A COPY OF THIS SPECIFICATION, PRODUCT DATA PAGES, SAFETY DATA PAGES, SURFACE PREPARATION STANDARDS AND MANUFACTURER’S RECOMMENDATIONS SHALL BE

KEPT ON SITE.

2) APPLICATOR SHALL PROVIDE AND UTILIZE WET AND DRY FILM THICKNESS, TEMPERATURE AND HUMIDITY GAUGES AS REQUIRED BY THE PERFORMANCE OF THE WORK.

3) COATINGS FOREMAN SHALL INSPECT AND MONITOR THE WORK OF PAINTERS AND BLASTERS UNDER HIS/HER DISCRETION.

4) THE APPLICATOR Q/A IS RESPONSIBLE FOR ALL CONTRACTED SCOPE OF WORK. MANUFACTURES REP IS TO ACT IN A CONSULTATIVE ROLE, MAKING CORRECTIVE

RECOMMENDATION ACTIONS AS NEEDED THROUGH TO COURSE OF THE APPLICATION. MANUFACTURER CANNOT BE HELD RESPONSIBLE FOR INCOMPLETE SCOPE OR

INADEQUATE PREPARATION AS WRITTEN.

MATERIAL ESTIMATE FOR FULL SCOPE OF WORK

COLOR PRODUCT DESCRIPTION UNIT SIZE MEAN DFT COVERAGE BATCHES ~ FOOTAGE

ESTIMATED

MATERIAL

RED SEAGUARD 5000 EPOXY 5-GAL KIT 140 SIFT / GAL @ 6.0DFT ~2,610 30 GALLONS

GRAY SEAGUARD 5000 EPOXY 5-GAL KIT 140 SQFT / GAL @ 6.0DFT ~5,220 100 GALLONS

WHITE SEAGUARD 5000 EPOXY 5-GAL KIT 140 SQFT / GAL @ 6.0DFT ~5,720 50 GALLONS

YELLOW SEAGUARD TIE COAT 5-GAL KIT 140 SQFT / GAL @ 6.0DFT N/A ~2,610 25 GALLONS

RED SEAGUARD ABLATIVE AF 5-GAL PAIL 146 SQFT / GAL @ 5.0 DFT ~2,610 25 GALLONS

BLACK SEAGUARD ABLATIVE AF 5-GAL PAIL 146 SQFT / GAL @ 5.0 DFT ~2,610 25 GALLONS

26373 SHERLOXANE 800 5-GAL KIT 202 SQFT / GAL @ 5.0 DFT ~2,610 20 GALLONS

WHITE (Markings) SHERLOXANE 800 1.25-GAL KIT 202 SQFT / GAL @ 5.0 DFT NA 2.5 GALLONS

TBD (WAIST

COLLAR)

SHERLOXANE 800 1.25-GAL KIT 202 SQFT / GAL @ 5.0 DFT ~800 5 GALLONS

REDUCERS

5000 REDUCERS R7K130 5-GAL PAIL < 10% REDUCTION NA 15 GALLONS

TIE-COAT REDUCER MEK 5-GAL PAIL < 10% REDUCTION N/A NA 10 GALLONS

AF REDUCER VM&P NAPTHA 5-GAL PAIL < 5% REDUCTION NA 10 GALLONS

800 CLEAN-UP MEK NA 10 GALLONS

NONSKID 36 MESH ALUMINUM OXIDE 50LB BAG 500 SQ/FT PER BAG ~2,080 5 BAGS

• ABOVE IS ESTIMATED BASED ON FULL SCOPE OF WORK. COVERAGE RATES MAY VARY GREATLY DUE TO APPLICATOR, WEATHER CONDITIONS

AND WASTE. THIS IS MEANT TO BE A GUIDELINE ONLY.

• ALL ESTIMATED GALLONS INCLUDE A 30% SPRAY LOSS FACTOR IN THE ESTIMATE

• ESTIMATES ARE FOR THE BARGE “CAMBRIDGE” AND “BALTIMORE”. BARGE “CHESAPEAKE” WILL HAVE THE SAME MATERIAL ESTIMATES MINUS

MATERIAL FOR WAIST COLLAR.

• MATERIAL ESTIMATES TO BE VERIFIED BY SHIPYARD. SHERWIN WILLIAMS MARINE DIVISION IS NOT RESPONSIBLE FOR ANY DISCREPANCIES IN

SQUARE FOOTAGE OR GALLON ESTIMATES

• COLOR OF FREEBOARD “FEDERAL STANDARD 26373 LIGHT GRAY” TO BE CONFIRMED FOR FREEBOARD, DECK AND WAIST COLLAR.

REPORT COMPLETED BY:

DAVID G. NORWICZ – DEDICATED MARINE COATINGS REPRESENTATIVE

Cell: 443.350.1707 E-mail: David.G.Norwicz@Sherwin.com

SEAGUARD® 5000 HS

EPOXY

P A N11B350 B P A N11B357 C U B P A N11W350 O W P A N11W357 C U O W P A N11R350 R P A N11R357 C U R P A N11A350 G P A N11A357 C U G P A N11H350 B P A N11H357 C U B P B N11V350 H

Protective

Marine Coatings

9.40Revised: November 4, 2021 www.sherwin-williams.com/protective

P D SEAGUARD 5000 HS EPOXY is a high performance and high solids, polyamine cured epoxy that is designed to be used as a part of an anticorrosive system for marine applications, or as a lining system for fuel, brine, ballast and non-potable water tanks.

• Complies with IMO Performance Standard for Protective Coatings SOLAS REGULATIONS II-1/3-2 and XII/6.3

• Corrosion resistant

• Outstanding adhesion

• Qualifi ed to MIL-PRF-24647 for underwater hull

• Qualifi ed to MIL-PRF-23236 for ballast tanks and fuel tanks

P C Finish: Low Sheen Color: Black, Off White, Red, Gray, and Buff Volume Solids: 73% ± 2% mixed Weight Solids: 79% ± 2% mixed VOC (EPA Method 24): <250 g/L; 2.08 lb/gal Mix Ratio: 1:1 by volume (2 components)

Recommended Spreading Rate per coat:

Minimum Maximum

Wet mils (microns) 7.0 (175) 10.0 (250) Dry mils (microns) 5.0 (125) 7.0 (175) ~Coverage sq ft/gal (m2/L) 167 (4.1) 234 (5.7) Theoretical coverage sq ft/gal (m2/L) @ 1 mil / 25 microns dft 1168 (28.6)

NOTE: Brush or roll application may require multiple coats to achieve maximum fi lm thickness and uniformity of appearance.

Drying Schedule @ 7.0 mils wet (175 microns):

35°F/1.7°C

50°F/10°C

77°F/25°C

110°F/43°C

50% RH

To touch: 8 hours 5 hours 4 hours 2 hours To recoat:

minimum: 24 hours 12 hours 6 hours 3 hours maximum*: 90 days 90 days 90 days 90 days

To cure: 20 days 14 days 7 days 7 days *Two weeks maximum for alkyd and urethane topcoats.

If maximum recoat time is exceeded, abrade surface before recoating.

Drying time is temperature, humidity, and fi lm thickness dependent.

Pot Life: 8 hours 6 hours 2 hours 1 hour Sweat-in-Time: None None None None Application of the antifouling coating shall occur while the epoxy coat is still tacky. Refer to the Application Bulletin for the defi nition of "TACKY".

Shelf Life: 36 months, unopened Store indoors at 40°F (4.5°C) to 100°F (38°C)

Flash Point (ADMIX): 110°F (43°C) PMCC Reducer: Not recommended* Clean Up: Reducer #130 (R7K130) *Contact your Sherwin-Williams representative for more information continued on back

R U For use as a coating for:

• Fuel, brine, ballast and non-potable water tanks

• Underwater hull with appropriate antifouling paint

• Interior or exterior marine applications

• Immersion service

• Freeboard, topside, decks

• Acceptable for use with UHP / waterjetted substrates

• Use N11-350 series for Military/Government vessels or which require IMO PSPC approval

• Use N11-357 series for commercial vessels

P C

Substrate*: Steel Surface Preparation*: SSPC-SP10/NACE 2 System Tested*:

2 cts. SeaGuard 5000 HS Epoxy @ 5.0 mils (125 microns) dft/ct *unless otherwise noted below

Test Name Test Method Results Solvent Resistance ASTM D1308 Passed

Qualifi ed to MIL-PRF-23236, Type VI, Class 5 and 7, Grade C

Qualifi ed to MIL-PRF-24647, Type I, Class 1 and 2, Grade A and B, Application 1, 2 and 4

Qualifi ed to MIL-PRF-24647, Type II, Class 1, Grade A and B, Application 1, 2, 3 and 4

Tested by Det Norske Veritas (DNV). According to DNV Procedure, testing and classifi cation of ballast tank coatings, REV-02. Tested to the DNV Procedure over a Zinc Shop Primer Steel.

Received Highest Obtainable rating B1

Epoxy coatings may darken or yellow following application and curing.

P A N11B350 B P A N11B357 C U B P A N11W350 O W P A N11W357 C U O W P A N11R350 R P A N11R357 C U R P A N11A350 G P A N11A357 C U G P A N11H350 B P A N11H357 C U B P B N11V350 H

Protective

Marine Coatings

9.40Revised: November 4, 2021 www.sherwin-williams.com/protective

S P Surface must be clean, dry, and in sound condition. Remove all oil, dust, grease, dirt, loose rust, and other foreign material to ensure adequate adhesion.

Refer to product Application Bulletin for detailed surface prepara-tion information.

Minimum recommended surface preparation:

Immersion:

Iron & Steel / Aluminum SSPC-SP10/NACE 2, 2.0 mil (50 micron) profi le or NACE/SSPC WJ2(M) – with existing surface anchor profi le of >2.0 mils (>50 microns) Atmospheric:

Iron & Steel / Aluminum minimum: SSPC-SP2, SSPC-SP3 preferred: SSPC-SP6/NACE 3, 2.0 mil (50 micron) profi le or NACE/SSPC WJ2(M) – with existing surface anchor profi le of >2.0 mils (>50 microns) Galvanizing: SSPC-SP1

Surface Preparation Standards Condition of Surface

ISO 8501-1

BS7079:A1

Swedish Std.

SIS055900 SSPC NACE

White Metal Sa 3 Sa 3 SP 5 1 Near White Metal Sa 2.5 Sa 2.5 SP 10 2 Commercial Blast Sa 2 Sa 2 SP 6 3 Brush-Off Blast Sa 1 Sa 1 SP 7 4 Hand Tool Cleaning Rusted C St 2 C St 2 SP 2 -

Pitted & Rusted D St 2 D St 2 SP 2 - Power Tool Cleaning Rusted C St 3 C St 3 SP 3 -

Pitted & Rusted D St 3 D St 3 SP 3 -

T Do not tint.

A C Temperature: 35°F (1.7°C) minimum, 110°F (43°C) maximum (air, surface, and material) At least 5°F (2.8°C) above dew point Relative humidity: 85% maximum Refer to product Application Bulletin for detailed application information.

O I Packaging:

Part A: 1 gallon (3.78L) and 5 gallon (18.9L) containers Part B: 1 gallon (3.78L) and 5 gallon (18.9L) containers Weight:

Part A: 12.73 ± 0.2 lb/gal; 1.5 Kg/L Part B: 11.43 ± 0.2 lb/gal; 1.4 Kg/L Mixed: 12.08 ± 0.2 lb/gal; 1.45 Kg/L

S P Refer to the SDS sheet before use.

Published technical data and instructions are subject to change without notice.

Contact your Sherwin-Williams representative for additional technical data and instructions.

W The Sherwin-Williams Company warrants our products to be free of manufactur-ing defects in accord with applicable Sherwin-Williams quality control procedures.

Liability for products proven defective, if any, is limited to replacement of the defec-tive product or the refund of the purchase price paid for the defective product as determined by Sherwin-Williams. NO OTHER WARRANTY OR GUARANTEE

OF ANY KIND IS MADE BY SHERWIN-WILLIAMS, EXPRESSED OR IMPLIED,

STATUTORY, BY OPERATION OF LAW OR OTHERWISE, INCLUDING MER-

CHANTABILITY AND FITNESS FOR A PARTICULAR PURPOSE.

P I R S

Dry Film Thickness / ct.

Mils (Microns) Steel or Aluminum, immersion:

2 cts. SeaGuard 5000 HS Epoxy 5.0-7.0 (125-175)

Steel or Aluminum, underwater hull:

2 cts. SeaGuard 5000 HS Epoxy 5.0-7.0 (125-175) 1-3 cts. SeaGuard Ablative Antifouling 2.5-4.0 (63-100) or 2 cts. SeaGuard 5000 HS Epoxy 4.0-8.0 (100-200) 2-3 cts. SeaVoyage Copper Free AF* 3.0-6.0 (75-150)

*SeaVoyage Copper Free Antifouling Paint must be applied over the epoxy primer, while the epoxy is still slightly tacky.

Steel or Aluminum, atmospheric:

1-2 cts. SeaGuard 5000 HS Epoxy 5.0-7.0 (125-175) 1-2 cts. Sherthane 2K 2.0-4.0 (50-100) or 1-2 cts. Polysiloxane XLE-80 HAPS Free 3.0-7.0 (75-175) or 1-2 cts. SeaGuard 1000 2.0-3.0 (50-75) or 1-2 cts. Hi-Solids Polyurethane 3.0-5.0 (75-125) Galvanized, atmospheric:

1 ct. SeaGuard 5000 HS Epoxy 4.0-7.0 (100-175) 1-2 cts. Sherthane 2K 2.0-4.0 (50-100) or 1-2 cts. Polysiloxane XLE-80 HAPS Free 3.0-7.0 (75-175) or 1-2 cts. SeaGuard 1000 2.0-3.0 (50-75) or 1-2 cts. Hi-Solids Polyurethane 3.0-5.0 (75-125)

Seawater Ballast Tank Applications In accordance with IMO Resolution MSC.215(82) PSPC, all application requirements specifi ed in PSPC Table 1 have to be strictly adhered to.

• Substrate: Abrasive blasting to Sa 2.5 (ISO 8501-1), SSPC-SP-10.

• Surface profi le: 30 - 75 microns as per ISO 8503-1/3.

• Water soluble contaminants: ≤ 50mg/m2 of sodium chloride. Conductivity measured in accordance with ISO 8502-9.

• Dry fi lm thickness: PSPC stipulates a Nominal Dry Film Thickness (NDFT) of 320 microns obtained in 2 coats. The fi lm thickness distribution is measured in accordance with the 90/10 rule.

• Maximum total dry fi lm thickness not to exceed 1000 mi-crons/40 mils.

• Coating sequence: Red, followed by light grey.

• Stripe coats: 2 strip coats in alternating colors must be ap-plied as part of the system.

The systems listed above are representative of the product's use, other systems may be appropriate.

D The information and recommendations set forth in this Product Data Sheet are based upon tests conducted by or on behalf of The Sherwin-Williams Company.

Such information and recommendations set forth herein are subject to change and pertain to the product off ered at the time of publication. Consult your Sherwin- Williams representative to obtain the most recent Product Data Information and Application Bulletin.

P A N11B350 B P A N11B357 C U B P A N11W350 O W P A N11W357 C U O W P A N11R350 R P A N11R357 C U R P A N11A350 G P A N11A357 C U G P A N11H350 B P A N11H357 C U B P B N11V350 H

Protective

Marine Coatings

9.40Revised: November 4, 2021 www.sherwin-williams.com/protective

S P

Surface must be clean, dry, and in sound condition. Remove all oil, dust, grease, dirt, loose rust, and other foreign material to ensure adequate adhesion.

Iron & Steel / Aluminum, Immersion Service:

Remove all oil and grease from surface by Solvent Cleaning per SSPC-SP1. Minimum surface preparation is Near White Metal Blast Cleaning per SSPC-SP10/NACE 2, or NACE/SSPC WJ2(M).

For SSPC-SP10/NACE 2, blast clean all surfaces using a sharp, angular abrasive for optimum surface profi le (2.0 mils / 50 microns).

For NACE/SSPC WJ2(M), the existing surface anchor profi le should be >2.0 mils (>50 microns). Remove all weld spatter and round all sharp edges. Prime any bare steel the same day as it is cleaned.

Iron & Steel / Aluminum, Atmospheric Service:

Minimum surface preparation is Hand Tool Clean per SSPC-SP2.

For surfaces prepared by SSPC-SP2, fi rst remove all oil and grease from surface by Solvent Cleaning per SSPC-SP1. For better performance, use Commercial Blast Cleaning per SSPC-SP6/ NACE 3, or NACE/SSPC WJ2(M). For SSPC-SP6/NACE 3, blast clean all surfaces using a sharp, angular abrasive for optimum sur-face profi le (2.0 mils / 50 microns). For NACE/SSPC WJ2(M), the existing surface anchor profi le should be >2.0 mils (>50 microns).

Prime any bare steel the same day as it is cleaned.

Galvanized Steel:

Allow to weather a minimum of six months prior to coating. Solvent Clean per SSPC-SP1 (recommended solvent is VM&P Naphtha).

When weathering is not possible, or the surface has been treated with chromates or silicates, fi rst Solvent Clean per SSPC-SP1 and apply a test patch. Allow paint to dry at least one week before test-ing adhesion. If adhesion is poor, brush blasting per SSPC-SP7 is necessary to remove these treatments. Rusty galvanizing requires a minimum of Hand Tool Cleaning per SSPC-SP2, prime the area the same day as cleaned.

Previously Painted Surfaces If in sound condition, clean the surface of all foreign material.

Smooth, hard or glossy coatings and surfaces should be dulled by abrading the surface. Apply a test area, allowing paint to dry one week before testing adhesion. If adhesion is poor, or if this product attacks the previous fi nish, removal of the previous coating may be necessary. If paint is peeling or badly weathered, clean surface to sound substrate and treat as a new surface as above.

Surface Preparation Standards Condition of Surface

ISO 8501-1

BS7079:A1

Swedish Std.

SIS055900 SSPC NACE

White Metal Sa 3 Sa 3 SP 5 1 Near White Metal Sa 2.5 Sa 2.5 SP 10 2 Commercial Blast Sa 2 Sa 2 SP 6 3 Brush-Off Blast Sa 1 Sa 1 SP 7 4 Hand Tool Cleaning Rusted C St 2 C St 2 SP 2 -

Pitted & Rusted D St 2 D St 2 SP 2 - Power Tool Cleaning Rusted C St 3 C St 3 SP 3 -

Pitted & Rusted D St 3 D St 3 SP 3 -

A B A C

Temperature: 35°F (1.7°C) minimum, 110°F (43°C) maximum (air, surface, and material) At least 5°F (2.8°C) above dew point

Relative humidity: 85% maximum

A E

The following is a guide. Changes in pressures and tip sizes may be needed for proper spray characteristics. Always purge spray equipment before use with listed reducer. Any reduction must be compliant with existing VOC regulations and compatible with the existing environmental and application conditions.

Reducer ............................Not recommended* Clean Up ..........................Reducer #130, R7K130

Airless Spray Pressure.........................2400 psi Hose...............................1/4" ID Tip ...................................017" - .031" Filter ...............................60 mesh Reduction .......................Not recommended*

Brush Brush..............................Natural Bristle Reduction .......................Not recommended*

Roller Cover .............................3/8" - 1/2" woven with solvent resistant core Reduction .......................Not recommended*

*Contact your Sherwin-Williams representative for more information

If specifi c application equipment is not listed above, equivalent equipment may be substituted.

continued on back

P A N11B350 B P A N11B357 C U B P A N11W350 O W P A N11W357 C U O W P A N11R350 R P A N11R357 C U R P A N11A350 G P A N11A357 C U G P A N11H350 B P A N11H357 C U B P B N11V350 H

Protective

Marine Coatings

9.40Revised: November 4, 2021 www.sherwin-williams.com/protective

A B A P

Surface preparation must be completed as indicated.

Mix contents of each component thoroughly with low speed power agitation. Make certain no pigment remains on the bottom of the cans. Then combine one part by volume of Part A with one part by volume of Part B. Thoroughly agitate the mixture with power agitation. Re-stir before using.

Apply paint at the recommended fi lm thickness and spreading rate as indicated below:

Recommended Spreading Rate per coat:

Minimum Maximum

Wet mils (microns) 7.0 (175) 10.0 (250) Dry mils (microns) 5.0 (125) 7.0 (175) ~Coverage sq ft/gal (m2/L) 167 (4.1) 234 (5.7) Theoretical coverage sq ft/gal (m2/L) @ 1 mil / 25 microns dft 1168 (28.6)

NOTE: Brush or roll application may require multiple coats to achieve maximum fi lm thickness and uniformity of appearance.

Drying Schedule @ 7.0 mils wet (175 microns):

35°F/1.7°C

50°F/10°C

77°F/25°C

110°F/43°C

50% RH

To touch: 8 hours 5 hours 4 hours 2 hours To recoat:

minimum: 24 hours 12 hours 6 hours 3 hours maximum*: 90 days 90 days 90 days 90 days

To cure: 20 days 14 days 7 days 7 days *Two weeks maximum for alkyd and urethane topcoats.

If maximum recoat time is exceeded, abrade surface before recoating.

Drying time is temperature, humidity, and fi lm thickness dependent.

Pot Life: 8 hours 6 hours 2 hours 1 hour Sweat-in-Time: None None None None Application of the antifouling coating shall occur while the epoxy coat is still tacky. Refer to the Application Bulletin for the defi nition of "TACKY".

Application of coating above maximum or below minimum recommended spreading rate may adversely aff ect coating performance.

C U I Clean spills and spatters immediately with Reducer #130, R7K130.

Clean tools immediately after use with Reducer #130, R7K130.

Follow manufacturer's safety recommendations when using any solvent.

D The information and recommendations set forth in this Product Data Sheet are based upon tests conducted by or on behalf of The Sherwin-Williams Company.

Such information and recommendations set forth herein are subject to change and pertain to the product off ered at the time of publication. Consult your Sherwin- Williams representative to obtain the most recent Product Data Information and Application Bulletin.

P T Stripe coat all crevices, welds, and sharp angles to prevent early failure in these areas.

When using spray application, use a 50% overlap with each pass of the gun to avoid holidays, bare areas, and pinholes. If necessary, cross spray at a right angle.

Spreading rates are calculated on volume solids and do not include an application loss factor due to surface profi le, roughness or po-rosity of the surface, skill and technique of the applicator, method of application, various surface irregularities, material lost during mixing, spillage, overthinning, climatic conditions, and excessive fi lm build.

Excessive fi lm build, poor ventilation, and cool temperatures may cause solvent entrapment and premature coating failure.

For Immersion Service: (if required) Holiday test in accordance with ASTM D5162 for steel, or ASTM D4787 for concrete.

Do not apply the material beyond recommended pot life.

Do not mix previously catalyzed material with new.

In order to avoid blockage of spray equipment, clean equipment before use or before periods of extended downtime with Reducer #130, R7K130.

Material must be at least 50°F/10°C prior to catalyzing.

Application of the antifoulant coating shall occur when the last coat of epoxy anticorrosive is still tacky. If the epoxy is hard, apply a tack coat of epoxy anticorrosive at 1-2 mils (25-50 microns) WFT over previously painted surfaces. "Tacky" is defi ned as that curing (drying) stage when a fi ngertip pressed lightly against the fi lm leaves only a slight impression and none of the fi lm sticks to the fi nger.

Application of solvent based alkyd coating, such as MIL-PRF-24635, shall be applied when the epoxy is "dry to the touch, but not fully cured." (For example prior to 7 days @ 77°F/25°C).

Refer to Product Information sheet for additional performance characteristics and properties.

S P Refer to the SDS sheet before use.

Published technical data and instructions are subject to change without notice.

Contact your Sherwin-Williams representative for additional technical data and instructions.

W The Sherwin-Williams Company warrants our products to be free of manufacturing defects in accord with applicable Sherwin-Williams quality control procedures.

Liability for products proven defective, if any, is limited to replacement of the de-fective product or the refund of the purchase price paid for the defective product as determined by Sherwin-Williams. NO OTHER WARRANTY OR GUARANTEE

OF ANY KIND IS MADE BY SHERWIN-WILLIAMS, EXPRESSED OR IMPLIED,

STATUTORY, BY OPERATION OF LAW OR OTHERWISE, INCLUDING MER-

CHANTABILITY AND FITNESS FOR A PARTICULAR PURPOSE.

SEAGUARD® ABLATIVE

ANTIFOULING COATING

P30RQ10 ................. R

P30BQ12 ............. B P30LQ13 ......................B

Protective

Marine Coatings

9.12Revised: June 9, 2020 www.sherwin-williams.com/protective

P D SEAGUARD ABLATIVE ANTIFOULING COATING is an advanced antifouling coating based on a polyamide polymer containing cu-prous oxide. Recommended for the underwater surfaces of steel vessels operating in all coastal and oceanic waters. This product maintains an eff ective, bio-active surface during its entire life.

• Long Life

• Brush, roll, or spray application

• A tin-free ablative coating

• Complies with the requirements of MIL-PRF-24647

P C Finish: Flat

Color: Red, Black, and Blue

Volume Solids: 65% ± 2%

VOC (EPA Method 24): <400 g/L; 3.33 lb/gal, maximum

Recommended Spreading Rate per coat:

Minimum Maximum

Wet mils (microns) 4.0 (100) 7.0 (175) Dry mils (microns) 2.5 (63) 4.0 (100) ~Coverage sq ft/gal (m2/L) 260 (6.4) 430 (10.5) Theoretical coverage sq ft/gal (m2/L) @ 1 mil / 25 microns dft 1040 (25.5)

NOTE: Brush or roll application may require multiple coats to achieve maximum fi lm thickness and uniformity of appearance.

Drying Schedule @ 5.0 mils wet (125 microns):

30°F/-1.1°C 50°F/10°C 70°F/21°C 85°F/29°C 100°F/38°C

50% RH

To recoat:

minimum: 32 hrs 16 hrs 8 hrs 4 hrs 2 hrs Undocking*: 48 hrs 24 hrs 12 hrs 8 hrs 4 hrs No maximum recoat time; however, any contamination must be removed by high pressure washing prior to applying the next coat.

*Undocking:

Minimum: depends on the number of coats applied, fi lm thickness, and temperature.

Maximum: depends on the exposure conditions. Refer to Performance Tips section for details.

Shelf Life: 36 months, unopened Store indoors at 40°F (4.5°C) to 100°F (38°C)

Flash Point: 72°F (22°C), SETA Flash Reducer/Clean Up: VM&P Naphtha, R1K3 continued on back

R U For use on prepared surfaces in marine environments

• As an antifoulant for underwater hull and boot top on vessels operating in global trade with short to medium idle times.

• Suitable for a wide range of operating environments and speeds

P C

• Resists fouling

• Contains 49% Cuprous Oxide

• Colors:

Red P30RQ10 Black P30BQ12 Blue P30LQ13

P30RQ10 ................. R

P30BQ12 ............. B P30LQ13 ......................B

Protective

Marine Coatings

9.12Revised: June 9, 2020 www.sherwin-williams.com/protective

S P

Surface must be clean, dry, and in sound condition. Remove all oil, dust, grease, dirt, loose rust, and other foreign material to ensure adequate adhesion.

Refer to product Application Bulletin for detailed surface prepara-tion information.

Minimum recommended surface preparation:

Iron & Steel, bare: SSPC-SP10/NACE 2 (For anticorrosive primer coat) Previously Painted: Clean, dry, sound

Surface Preparation Standards Condition of Surface

ISO 8501-1

BS7079:A1

Swedish Std.

SIS055900 SSPC NACE

White Metal Sa 3 Sa 3 SP 5 1 Near White Metal Sa 2.5 Sa 2.5 SP 10 2 Commercial Blast Sa 2 Sa 2 SP 6 3 Brush-Off Blast Sa 1 Sa 1 SP 7 4 Hand Tool Cleaning Rusted C St 2 C St 2 SP 2 -

Pitted & Rusted D St 2 D St 2 SP 2 - Power Tool Cleaning Rusted C St 3 C St 3 SP 3 -

Pitted & Rusted D St 3 D St 3 SP 3 -

T Do not tint.

A C

• Maximum application temperature is 120°F (49°C)

• Surface temperature must be at least 5°F (2.8°C) above the dew point

• No surface ice, moisture, or condensation may be allowed on the surface during application

O I Packaging: 5 gallon (18.9L) containers

Weight: 18.5 ± lb/gal ; 2.22 Kg/L

S P Refer to the SDS sheet before use.

Published technical data and instructions are subject to change without notice.

Contact your Sherwin-Williams representative for additional technical data and instructions.

W The Sherwin-Williams Company warrants our products to be free of manufactur-ing defects in accord with applicable Sherwin-Williams quality control procedures.

Liability for products proven defective, if any, is limited to replacement of the defec-tive product or the refund of the purchase price paid for the defective product as determined by Sherwin-Williams. NO OTHER WARRANTY OR GUARANTEE

OF ANY KIND IS MADE BY SHERWIN-WILLIAMS, EXPRESSED OR IMPLIED,

STATUTORY, BY OPERATION OF LAW OR OTHERWISE, INCLUDING MER-

CHANTABILITY AND FITNESS FOR A PARTICULAR PURPOSE.

P I R S

Dry Film Thickness / ct.

Mils (Microns) Steel:

2 cts. SeaGuard 5000 HS 5.0 -7.0 (125-175) 1-3 cts. SeaGuard Ablative Antifouling 2.5-4.0 (63-100) NOTE: Number of coats is dependent on specifi cation, existing hull conditions, and intended service life.

Steel:

2 cts. Macropoxy 646 PW 5.0-7.0 (125-175) 1-3 cts. SeaGuard Ablative Antifouling 2.5-4.0 (63-100) NOTE: Number of coats is dependent on specifi cation and intended service life.

Previously Painted:

1-3 cts. SeaGuard Ablative Antifouling 2.5-4.0 (63-100) NOTE: Number of coats is dependent on specifi cation, existing hull conditions, and intended service life.

The systems listed above are representative of the product's use, other systems may be appropriate.

D The information and recommendations set forth in this Product Data Sheet are based upon tests conducted by or on behalf of The Sherwin-Williams Company.

Such information and recommendations set forth herein are subject to change and pertain to the product off ered at the time of publication. Consult your Sherwin-

P30RQ10 ................. R

P30BQ12 ............. B P30LQ13 ......................B

Protective

Marine Coatings

9.12Revised: June 9, 2020 www.sherwin-williams.com/protective

S P

Surface must be clean, dry, and in sound condition. Remove all oil, dust, grease, dirt, loose rust, and other foreign material to ensure adequate adhesion.

Iron & Steel, bare Minimum surface preparation is Near White Metal Blast per SSPC-SP10/NACE 2. Remove all oil and grease from surface by Solvent Cleaning per SSPC-SP1. Blast clean all surfaces using a sharp, angular abrasive for optimum surface profile (2 mils / 50 microns). Remove all weld spatter and round all sharp edges by grinding. For surfaces prepared per waterjet cleaning, all surfaces to be coated shall be cleaned in accordance with SSPC-SP WJ-2 L, Very Thorough Cleaning, Light Flash Rust. Pre-existing profile should be approximately 2 mils (50 microns).

Previously Painted Antifouling Surfaces Remove possible oil, grease, etc. with suitable detergent.

Rinse using high pressure, fresh water cleaning, which will also remove any weak, outer layer of leached antifouling.

Allow the surface to dry before overcoating.

Whether or not to use a sealer coat over an existing antifouling depends on the type and condition of the existing antifouling.

Surface Preparation Standards Condition of Surface

ISO 8501-1

BS7079:A1

Swedish Std.

SIS055900 SSPC NACE

White Metal Sa 3 Sa 3 SP 5 1 Near White Metal Sa 2.5 Sa 2.5 SP 10 2 Commercial Blast Sa 2 Sa 2 SP 6 3 Brush-Off Blast Sa 1 Sa 1 SP 7 4 Hand Tool Cleaning Rusted C St 2 C St 2 SP 2 -

Pitted & Rusted D St 2 D St 2 SP 2 - Power Tool Cleaning Rusted C St 3 C St 3 SP 3 -

Pitted & Rusted D St 3 D St 3 SP 3 -

A B A C

• Maximum application temperature is 120°F (49°C)

• Surface temperature must be at least 5°F (2.8°C) above the dew point

• No surface ice, moisture, or condensation may be allowed on the surface during application

A E

The following is a guide. Changes in pressures and tip sizes may be needed for proper spray characteristics. Always purge spray equipment before use with listed reducer. Any reduction must be compliant with existing VOC regulations and compatible with the existing environmental and application conditions.

Reducer/Clean Up ...........VM&P Naphtha, R1K3

Airless Spray Pressure.........................3600 psi Hose...............................3/8" ID Tip ...................................023" - .027" Filter ...............................100 mesh Reduction .......................as needed up to 5% by volume

Brush Brush..............................Natural Bristle Reduction .......................as needed up to 5% by volume

Roller Cover .............................3/8" woven with solvent resistant core Reduction .......................as needed up to 5% by volume

If specifi c application equipment is not listed above, equivalent

P30RQ10 ................. R

P30BQ12 ............. B P30LQ13 ......................B

Protective

Marine Coatings

9.12Revised: June 9, 2020 www.sherwin-williams.com/protective

A B A P

Surface preparation must be completed as indicated.

Mixing Instructions: Mix paint thoroughly with low speed power agitation prior to use. Make sure there is no settling on the bottom of the can.

Apply paint at the recommended fi lm thickness and spreading rate as indicated below:

Recommended Spreading Rate per coat:

Minimum Maximum

Wet mils (microns) 4.0 (100) 7.0 (175) Dry mils (microns) 2.5 (63) 4.0 (100) ~Coverage sq ft/gal (m2/L) 260 (6.4) 430 (10.5) Theoretical coverage sq ft/gal (m2/L) @ 1 mil / 25 microns dft 1040 (25.5)

NOTE: Brush or roll application may require multiple coats to achieve maximum fi lm thickness and uniformity of appearance.

Drying Schedule @ 5.0 mils wet (125 microns):

30°F/-1.1°C 50°F/10°C 70°F/21°C 85°F/29°C 100°F/38°C

50% RH

To recoat:

minimum: 32 hrs 16 hrs 8 hrs 4 hrs 2 hrs Undocking*: 48 hrs 24 hrs 12 hrs 8 hrs 4 hrs No maximum recoat time; however, any contamination must be removed by high pressure washing prior to applying the next coat.

*Undocking:

Minimum: depends on the number of coats applied, fi lm thickness, and temperature.

Maximum: depends on the exposure conditions. Refer to Performance Tips section for details.

Application of coating above maximum or below minimum recommended spreading rate may adversely aff ect coating performance.

C U I Clean spills and spatters immediately with VM&P Naphtha, R1K3. Clean tools immediately after use with VM&P Naphtha, R1K3. Follow manufac-turer's safety recommendations when using any solvent.

D The information and recommendations set forth in this Product Data Sheet are based upon tests conducted by or on behalf of The Sherwin-Williams Company.

Such information and recommendations set forth herein are subject to change and pertain to the product off ered at the time of publication. Consult your Sherwin- Williams representative to obtain the most recent Product Data Information and Application Bulletin.

P T When using spray application, use a 50% overlap with each pass of the gun to avoid holidays, bare areas, and pinholes. If necessary, cross spray at a right angle

Spreading rates are calculated on volume solids and do not include an application loss factor due to surface profi le, roughness or porosity of the surface, skill and technique of the applicator, method of application, various surface irregularities, material lost during mixing, spillage, overthinning, climatic conditions, and excessive fi lm build.

Excess reduction of material is not recommended as it can aff ect fi lm build, appearance, and adhesion.

In order to avoid blockage of spray equipment, clean equipment before use or before periods of extended downtime with VM&P Naphtha, R1K3.

When applying over the recommended epoxy coat, the epoxy shall be tacky, but not hard. "Tacky" is defi ned as that curing (drying) stage when a fi ngertip pressed lightly against the fi lm leaves only a slight impression and none of the fi lm sticks to the fi nger.

By providing a constantly active surface during its lifetime, this antifouling is gradually sacrifi ced in the process. The color of the system changes in accordance with the colors of the coats applied, e. g.: Light red changes to whitish in direct contact with seawater.

Indicated fi lm thickness will vary according to specifi cation. This will alter spreading rate and may infl uence drying time. In case of multi-coat applica-tion, drying time and minimum overcoating interval will be infl uenced by the number of coats and by the thickness of each coat applied.

Overcoating: No maximum overcoating interval, but after prolonged expo-sure to polluted atmosphere, remove accumulated contamination by high pressure fresh water cleaning and allow to dry before applying next coat.

Undocking: Minimum undocking time depends on number of coats applied, fi lm thickness, and the prevailing temperature.

Maximum undocking time depends on the exposure conditions, degree of air pollution, etc. The most important factor is to carry out a thorough high pressure fresh water cleaning after prolonged exposure. Outfi tting of up to 6 months followed by such cleaning normally presents no problem. Longer outfi tting periods to be evaluated from case to case. The recommended maximum undocking interval relates to vertical bottom only. Flat bottom, which has not been exposed to direct sunlight, will for all normal practical building schedules have a no-maximum value.

Refer to Product Information sheet for additional performance charac-teristics and properties.

S P Refer to the SDS sheet before use.

Published technical data and instructions are subject to change without notice.

Contact your Sherwin-Williams representative for additional technical data and instructions.

W The Sherwin-Williams Company warrants our products to be free of manufacturing defects in accord with applicable Sherwin-Williams quality control procedures.

Liability for products proven defective, if any, is limited to replacement of the de-fective product or the refund of the purchase price paid for the defective product as determined by Sherwin-Williams. NO OTHER WARRANTY OR GUARANTEE

OF ANY KIND IS MADE BY SHERWIN-WILLIAMS, EXPRESSED OR IMPLIED,

SEAGUARD® TIE COAT

P A P23Y00001 Y P B P23V00001 H

Protective

Marine Coatings

Revised: November 4, 2021 www.sherwin-williams.com/protective

P D SEAGUARD TIE COAT is an epoxy developed to enhance adhesion of anti-foulants. SeaGuard Tie Coat has an extended overcoat window for anti-foulant application. This eliminates the requirements for a "tacky" epoxy onto which to apply anti-foulant.

P C Finish: Flat

Color: Yellowish-Gray

Volume Solids: 62% ± 1%, mixed

VOC (EPA Method 24): 340 g/L; 2.8 lb/gal, mixed

Mix Ratio: 7A:1B, by volume

Recommended Spreading Rate per coat:

Minimum Maximum

Wet mils (microns) 6.0 (150) 12.0 (300) Dry mils (microns) 4.0 (100) 8.0 (200) ~Coverage sq ft/gal (m2/L) 124 (3.0) 249 (6.1) Theoretical coverage sq ft/gal (m2/L) @ 1 mil / 25 microns dft 995 (25)

NOTE: Brush or roll application may require multiple coats to achieve maximum fi lm thickness and uniformity of appearance.

Drying Schedule @ 8.0 mils wet (200 microns):

@ 50°F/10°C @ 68°F/20°C @ 86°F/30°C

To handle: 10 hours 6 hours 5 hours To recoat:

minimum: 11 hours 5.5 hours 4 hours maximum: 7 days 3.5 days 3 days

To cure: 7 days NOTE: The fi lm must be dry (not tacky) before application of subse-quent coats and all minimum overcoating intervals must be observed.

If maximum recoat time is exceeded, abrade surface before recoating.

Drying time is temperature, humidity, and fi lm thickness dependent.

Pot Life: 3.5 hours 2 hours 1 hour

Shelf Life: 36 months, unopened Store indoors at 40°F (4°C) to 100°F (38°C).

Flash Point: 70°F (21°C), mixed Clean Up: MAK or MEK continued on back

R U For use on marine vessels and structures

• As second coat of an epoxy underwater hull system

• Not required to be "tacky" when applying anti-foulant

• Qualifi ed to MIL-PRF-24647E, Type I, Class 1 & 2, Grade A, Application 1, 2, 4

• Qualifi ed to MIL-PRF-24647E, Type II, Class 1, Grade A, Application 1, 2, 3, 4

• For use as a "sealer" for existing anti-foulant systems

P B P23V00001 H

Protective

Marine Coatings

Revised: November 4, 2021 www.sherwin-williams.com/protective

S P Surface must be clean, dry, and in sound condition. Remove all oil, dust, grease, dirt, loose rust, and other foreign material to ensure adequate adhesion.

Refer to product Application Bulletin for detailed surface prepara-tion information.

Minimum recommended surface preparation:

Iron & Steel: SSPC-SP10/NACE 2

Surface Preparation Standards Condition of Surface

ISO 8501-1

BS7079:A1

Swedish Std.

SIS055900 SSPC NACE

White Metal Sa 3 Sa 3 SP 5 1 Near White Metal Sa 2.5 Sa 2.5 SP 10 2 Commercial Blast Sa 2 Sa 2 SP 6 3 Brush-Off Blast Sa 1 Sa 1 SP 7 4 Hand Tool Cleaning Rusted C St 2 C St 2 SP 2 -

Pitted & Rusted D St 2 D St 2 SP 2 - Power Tool Cleaning Rusted C St 3 C St 3 SP 3 -

Pitted & Rusted D St 3 D St 3 SP 3 -

T Do not tint.

A C

• Use only where application and curing can proceed at temperatures above 23°F (-5°C). The temperature of the surface and that of the paint itself must also be above this limit.*

• When the ambient temperature is below 59°F (15°C), then the paint should be kept above 68°F (20°C)

• Apply only on a dry and clean surface with a temperature above the dew point to avoid condensation

*While application down to -5°C/23°F is possible, curing (and full hardness) will take longer at lower temperatures.

O I Packaging:

Part A: 4.38 gallons (16.6L) in a 5 gallon (18.9L) pail Part B: 0.62 gallons (2.3L) in a 1 gallon (3.8L) container

Weight: 11.69 ± 0.2 lb/gal ; 1.4 Kg/L

S P Refer to the SDS sheet before use.

Published technical data and instructions are subject to change without notice.

Contact your Sherwin-Williams representative for additional technical data and instructions.

W The Sherwin-Williams Company warrants our products to be free of manufactur-ing defects in accord with applicable Sherwin-Williams quality control procedures.

Liability for products proven defective, if any, is limited to replacement of the defec-tive product or the refund of the purchase price paid for the defective product as determined by Sherwin-Williams. NO OTHER WARRANTY OR GUARANTEE

OF ANY KIND IS MADE BY SHERWIN-WILLIAMS, EXPRESSED OR IMPLIED,

STATUTORY, BY OPERATION OF LAW OR OTHERWISE, INCLUDING MER-

CHANTABILITY AND FITNESS FOR A PARTICULAR PURPOSE.

P I R S

Dry Film Thickness / ct.

Mils (Microns) Steel:

1 ct. SeaGuard 5000 HS 5.0-7.0 (125-175) 1 ct. SeaGuard Tie Coat 5.0-7.0 (125-175) 2-3 cts. SeaGuard Ablative AF 5.0-7.0 (125-175)

Steel:

1 ct. SeaGuard 5000 HS 5.0-7.0 (125-175) 1 ct. SeaGuard Tie Coat 5.0-7.0 (125-175) 2-3 cts. SeaVoyage Copper Free AF 5.0-7.0 (125-175)

The systems listed above are representative of the product's use, other systems may be appropriate.

D The information and recommendations set forth in this Product Data Sheet are based upon tests conducted by or on behalf of The Sherwin-Williams Company.

Such information and recommendations set forth herein are subject to change and pertain to the product off ered at the time of publication. Consult your Sherwin-

P B P23V00001 H

Protective

Marine Coatings

Revised: November 4, 2021 www.sherwin-williams.com/protective

S P

Surface must be clean, dry, and in sound condition. Remove all oil, dust, grease, dirt, loose rust, and other foreign material to ensure adequate adhesion.

Iron & Steel Minimum surface preparation is Near White Blast Cleaning per SSPC-SP10/NACE 2. For temporary protection, if required, use a suitable shop primer. All damage of shop primer and contamination from storage and fabrication should be thoroughly cleaned prior to fi nal painting.

Maintenance Remove oil and grease etc. thoroughly with suitable detergent.

Remove salts and other contaminants by high pressure fresh water cleaning. When used as "tiecoat": Remove all rust and loose material by abrasive blasting or power tool cleaning. Feather edges to sound and intact areas. Dust off residues. Touch up to full fi lm thickness. When used as “sealer” on old antifouling: a very thorough high pressure freshwater cleaning or jetting, if needed - to remove possible leached layer of antifouling and make sure that old layers of weak intercoat adhesion (“sandwich structure”) are removed.

Surface Preparation Standards Condition of Surface

ISO 8501-1

BS7079:A1

Swedish Std.

SIS055900 SSPC NACE

White Metal Sa 3 Sa 3 SP 5 1 Near White Metal Sa 2.5 Sa 2.5 SP 10 2 Commercial Blast Sa 2 Sa 2 SP 6 3 Brush-Off Blast Sa 1 Sa 1 SP 7 4 Hand Tool Cleaning Rusted C St 2 C St 2 SP 2 -

Pitted & Rusted D St 2 D St 2 SP 2 - Power Tool Cleaning Rusted C St 3 C St 3 SP 3 -

Pitted & Rusted D St 3 D St 3 SP 3 -

A B A C

• Use only where application and curing can proceed at temperatures above 23°F (-5°C). The temperature of the surface and that of the paint itself must also be above this limit.*

• When the ambient temperature is below 59°F (15°C), then the paint should be kept above 68°F (20°C)

• Apply only on a dry and clean surface with a temperature above the dew point to avoid condensation

*While application down to -5°C/23°F is possible, curing (and full hardness) will take longer at lower temperatures.

A E

The following is a guide. Changes in pressures and tip sizes may be needed for proper spray characteristics. Always purge spray equipment before use with listed reducer. Any reduction must be compliant with existing VOC regulations and compatible with the existing environmental and application conditions.

Clean Up ..........................MAK or MEK Reducer ............................Not required

Airless Spray Pressure.........................3335 psi Tip ..................................0.023"

Brush (touch up) ..............Natural Bristle

If specifi c application equipment is not listed above, equivalent

P B P23V00001 H

Protective

M…