80KSC026R0022 Attachment J-02 - NASA-STD-5008B.pdf

80KSC026R0022

NASA Rechargers

Attachment J-02

NASA-STD-5008B

KENNEDY SPACE CENTER

APPROVED FOR PUBLIC RELEASE — DISTRIBUTION IS UNLIMITED

METRIC/SI (ENGLISH)

NASA TECHNICAL STANDARD

NASA-STD-5008B

w/CHANGE 2:

REVALIDATED

2024-09-30 National Aeronautics and Space Administration

Approved: 2011-03-18 Superseding NASA-STD-5008A

PROTECTIVE COATING OF CARBON STEEL,

STAINLESS STEEL, AND ALUMINUM ON

LAUNCH STRUCTURES, FACILITIES, AND

GROUND SUPPORT EQUIPMENT

NASA-STD-5008B W/CHANGE 2

DOCUMENT HISTORY LOG

Status Document

Revision

Change

Number

Approval Date Description

Baseline 07-10-2001 Baseline Release.

Revision A 01-21-2004 See changes below.

Foreword: Changed signature of W. Brian Keegan to Theron M. Bradley. Updated Table of

Contents and KSC FORM 21-61ONS, Standardization Document Improvement Proposal.

General editorial/punctuation changes/corrections throughout document: put brackets inside parentheses and deleted “etc.” following “e.g.” Used non, free and proof as combining forms. Put a hyphen between Sherwin Williams. Changed Ameron International, P.C.G. to P.C.F.G. and web site to www.ameron.com. Changed Materials Science Division (LO-G) to Spaceport Technology

Development Office (YA-C2).

Added paragraph 1.6, Environmental stewardship.

Paragraph 2.2: Changed MIL-C-24667A to MIL-PRF-24667A. Deleted MIL-T-81772.

Paragraph 2.3: Changed title of ASTM A653 to Standard Specification for Steel Sheet, Zinc-Coated

(Galvanized) or Zinc-Iron Alloy-Coated (Galvannealed) by the Hot-Dip Process and changed the

ASTM address to 100 Barr Harbor Drive, West Conshohocken, PA 19482-2959. Changed the title of RP0188-88 to Discontinuity (Holiday) Testing of New Protective Coatings on Conductive

Substrates. Changed the title of SSPC SP 5-94, Joint Surface Preparation Standard, to SSPC-SP 5-

94/NACE No. 1, White Metal Blast Cleaning. Changed SSPC SP 10-94, Joint Surface Preparation

Standard Near-White Blast Cleaning, to SSPC-SP 10-00/NACE No. 2, Near-White Blast Cleaning.

Paragraph 3: Deleted AISC, American Institute of Steel Construction; cfm, cubic feet per minute;

GFE, Government-furnished equipment; and KHB, Kennedy handbook. Changed LO-G to YA-C2-

T. Added ASME, American Society of Mechanical Engineers; CFR, Code of Federal Regulations;

HAP, hazardous air pollutant; PDCA, Painting and Decorating Contractors of America; and YA-F, Labs and Testbed Division. Changed mega Pascal to megapascal.

Paragraph 4.1.2.4.e.2: Changed 235 to 239. Put parentheses around number listing.

Paragraph 4.1.4: Changed Materials and Chemical Analysis Laboratory to Spaceport Technology

Development Office.

Paragraph 4.3.1: Added “and NASA policies” to the end of the last sentence.

Revision

Change

Number

Approval Date Description

Revision

(Continued)

A 01-21-2004 See changes below.

4.4.1: Rewrote the first sentence. Added a sentence after the first sentence.

4.4.3.3 Added/environmental to safety/fire in the last sentence.

4.5.1: Added “An inorganic zinc coating used in a friction-type joint must be approved by the American Institute of Steel Construction (AISC),” after the fifth sentence.

Paragraph 5.7.5, end of the third sentence: Added “while considering the accuracy of the measurement instrument.”

Appendix A, Section I: Changed zip code for Ameron International, P.C.F.G to

92821.

Appendix A, Section II: Added Dimetcote D-9HS SB; SB to Cathacoat 304V;

Cathacoat 304H SB; and ZincClad IIHS SB to Coating Designations and Type.

Added InterZinc 22HS, SB, International Paint, 6001 Antoine Drive, Houston, TX

77091, (713) 682-1711, www.international-pc.com.

Appendix B, Section II: Added (SB) to Primer (Type) D-21-9. Added D-9HS (SB) to

Primer (Type) and PSX700(SB) to Topcoat (Type).

Appendix B, Section III: Added D-9HS (SB) and ZincClad IIHS (SB) to Primer

(Type). Added InterZinc 22HS (SB), 181 (SB) (IOT), International Paint, 6001

Antoine Drive, Houston, TX 77091, (713) 682-1711, www.international-pc.com.

Changed Topcoat (Type) 7551 P1 (SB) (IOT) to 5555.

Revision B

03/18/2011 General Revision: Changes are not listed; reader must review complete document.

1 2016-05-31 Revalidated w/Administrative/Editorial

Changes—This NASA Technical

Standard was reviewed and no technical changes resulted, but some requirements were clarified.

Administrative changes to number requirements, add a Requirements

Compliance Matrix as Appendix A, and conform to the current template were made, along with editorial corrections.

Revision

Change

Number

Approval Date Description

2 2024-09-30 Administrative change:

Revalidated – This NAA Technical

Standard is revalidated “as-is” pending revision to the document.

FOREWORD

This NASA Technical Standard is published by the National Aeronautics and Space

Administration (NASA) to provide uniform engineering and technical requirements for processes, procedures, practices, and methods that have been endorsed as standard for NASA programs and projects, including requirements for selection, application, and design criteria of an item.

This NASA Technical Standard is approved for use by NASA Headquarters and NASA Centers and Facilities and may be cited in contract, program, and other Agency documents as a technical requirement. It may also apply to the Jet Propulsion Laboratory and other contractors only to the extent specified or referenced in applicable contracts.

This NASA Technical Standard was developed to ensure the inclusion of essential criteria in the coating of ground support equipment (GSE) and facilities used by or for NASA.

This NASA Technical Standard establishes practices for the protective coating of GSE and related facilities used by or for NASA programs and projects. This NASA Technical Standard is for the design of nonflight hardware used to support the operations of receiving, transportation, handling, assembly, inspection, test, checkout, service, and launch of space vehicles and payloads at NASA launch, landing, or retrieval sites. These criteria and practices may be used for items used at the manufacturing, development, and test sites upstream of the launch, landing, or retrieval sites.

The information provided herein is recommended for use in the preparation of written, individual coating specifications for specific projects for the prevention of corrosion through the use of protective coatings on facilities, space vehicle launch structures, and GSE in all environments.

Requests for information should be submitted via “Feedback” at https://standards.nasa.gov.

Requests for changes to this NASA Technical Standard should be submitted via MSFC Form

4657, Change Request for a NASA Engineering Standard.

Original Signed By: 03/18/2011

Michael G. Ryschkewitsch Approval Date

NASA Chief Engineer https://standards.nasa.gov/

TABLE OF CONTENTS

SECTION PAGE

DOCUMENT HISTORY LOG

FOREWORD

TABLE OF CONTENTS

LIST OF APPENDICES

LIST OF TABLES

1. SCOPE

1.1 Purpose

1.2 Applicability

1.3 Tailoring

1.4 Zones of Exposure

1.5 Method of Specifying Coating Requirements

1.6 Environmental Stewardship and Health and Safety

2. APPLICABLE DOCUMENTS

2.1 General

2.2 Government Documents

2.3 Non-Government Documents

2.4 Order of Precedence

3. ACRONYMS AND DEFINITIONS

3.1 Acronyms, Abbreviations, and Symbols

3.2 Definitions

4. REQUIREMENTS

4.1 Materials

4.1.1 Abrasive-Blasting Aggregate

4.1.2 Protective Coatings, Thinners, and Cleaners

4.1.2.1 Inorganic Zinc Coatings

4.1.2.2 Primer and/or Intermediate Coatings

4.1.2.3 Finish Coatings

4.1.2.4 Epoxy Mastic Coatings

4.1.2.5 Coal Tar Epoxy

4.1.2.6 Potable Water Epoxy

4.1.2.7 Nonskid Coating

4.1.3 Sealants/Caulking

4.1.4 Chip-Free Clean-Room Paint

SECTION

TABLE OF CONTENTS (Continued)

PAGE

4.2 Equipment

4.2.1 Compressed Air

4.2.2 Abrasive-Blasting System

4.2.3 Coating Application System

4.2.4 Respiratory Protection

4.3 Safety and Health Requirements

4.3.1 Environmental Requirements

4.3.2 Personal Protective Equipment (PPE)

4.4 General Requirements

4.4.1 Applicator Qualifications

4.4.2 Preparation of Surfaces

4.4.2.1 Cleaning and Degreasing

4.4.2.2 Abrasive Blasting

4.4.2.3 Mechanical Cleaning Methods

4.4.3 Application of Coatings

4.4.3.1 Coating Systems

4.4.3.2 Colors

4.4.3.3 Storage of Coating Materials

4.4.3.4 Mixing and Application Instructions

4.4.3.5 Weather Conditions

4.4.3.6 Methods of Application

4.4.3.7 Coating Finish

4.4.3.8 Touchup of Welds and Damaged Coatings

4.4.3.9 Coating, Drying, and Curing

4.4.4 Sealing/Caulking

4.5 Specific Requirements

4.5.1 Protection of Carbon Steel

4.5.1.1 Protection with Inorganic Zinc

4.5.1.2 Protection by Galvanizing

4.5.1.3 Protection with Metallizing

4.5.2 Protection of Aluminum

4.5.2.1 Surface Preparation of Aluminum

4.5.2.2 Protective Coatings

4.5.3 Protection of Stainless Steel

4.5.3.1 Surface Preparation of Stainless Steel

4.5.3.2 Protective Coating

4.5.4 Underground, Submerged, or Continuously Wetted Surfaces

TABLE OF CONTENTS (Continued)

SECTION PAGE

4.5.5 Coatings Systems for Potable Water Immersion Service

4.5.6 Provision for Nonskid Surfaces

4.5.7 Coating Systems for Metallic Surfaces Under Thermal Insulation

4.5.8 Repair of Applied Coatings

4.5.9 Maintenance of Existing Coatings

5. QUALITY ASSURANCE PROVISIONS

5.1 Responsibility for Inspection

5.2 Requirements for Inspection

5.3 Inspection Hold Points

5.4 Inspection Forms

5.5 Inspection Prior to Surface Preparation and Coating Application

5.5.1 Surface Condition

5.5.2 Protection of Adjacent Surfaces

5.5.3 Ambient Weather Conditions

5.5.4 Compressed Air Cleanliness

5.5.5 Surface Salt Concentration

5.6 Surface Preparation Inspection

5.6.1 Abrasive-Blasting Material

5.6.2 Blast Nozzle Air Pressure and Size

5.6.3 Degree of Surface Cleanliness

5.6.4 Surface Profile or Roughness

5.6.5 Blasting of Abrasive-Sensitive Components

5.7 Coating Application Inspection

5.7.1 Surface Condition

5.7.2 Coating Materials

5.7.3 Storage of Coating Material

5.7.4 Mixing and Application of Coatings

5.7.5 Coating Finish and DFT

5.8 Caulking Inspection

5.9 Galvanizing Inspection

LIST OF APPENDICES

APPENDIX PAGE

A Approved Products List for Inorganic Zinc Coatings

B Approved Products List for Topcoat Systems

C Approved Products List for Metallized (TSC) Systems

D Coating Specification Key Elements

E Coating Schedule

F Coating System Daily Inspection Report

G Dry Film Thickness Measurement Worksheet

H Deliverables

I Guidance

J Requirements Compliance Matrix

TABLE

LIST OF TABLES

PAGE

1 Repair of Applied Coatings

PROTECTIVE COATING OF CARBON STEEL, STAINLESS

STEEL, AND ALUMINUM ON LAUNCH STRUCTURES,

FACILITIES, AND GROUND SUPPORT EQUIPMENT

1. SCOPE

1.1 Purpose

1.1.1 The purpose of this NASA Technical Standard is to establish requirements for the application of protective coatings to mitigate corrosion of exposed carbon steel, stainless steel, and aluminum.

1.1.2 This NASA Technical Standard provides a design standard for experienced corrosion control engineers for the development of specifications, including requirements for materials, equipment, safety, procedures, and quality assurance inspections.

1.1.3 Refer to section 1.2 for the intended use of this NASA Technical Standard and surfaces to be coated according to this NASA Technical Standard. Refer to Appendices A, B, and C for listings of approved coating materials.

1.2 Applicability

1.2.1 This NASA Technical Standard is applicable to facilities, launch structures, ground support equipment (GSE), test facilities, and structures that are intended for use at all NASA locations world-wide.

1.2.2 This NASA Technical Standard is approved for use by NASA Headquarters and NASA

Centers and Facilities and may be cited in contract, program, and other Agency documents as a technical requirement. It may also apply to the Jet Propulsion Laboratory and other contractors only to the extent specified or referenced in applicable contracts.

1.2.3 Verifiable requirements are numbered and indicated by the word “shall”; this NASA

Technical Standard contains 333 requirements. Explanatory or guidance text is indicated in italics beginning in section 4. To facilitate requirements selection and verification by NASA programs and projects, a Requirements Compliance Matrix is provided in Appendix J.

1.2.4 [PCR 1] This NASA Technical Standard shall be used in the preparation of written, individual coating specifications for specific projects for the prevention of corrosion through the use of protective coatings on space vehicle launch structures, facilities, GSE, and test facilities and structures in the specific environments identified in section 1.4.

1.2.5 [PCR 2] Due to the changing environmental considerations and different site conditions, new advances in corrosion technology, and a wide array of possible applications, this NASA Technical

Standard shall not be used as a stand-alone specification that meets every contingency.

1.2.6 [PCR 3] The appendices are considered to be an integral part of this NASA Technical

Standard. Appendices A, B, C, and D shall be used for the preparation of all coating specifications.

1.3 Tailoring

[PCR 4] Tailoring of this NASA Technical Standard for application to a specific program or project shall be formally documented as part of program or project requirements and approved by the Technical Authority in accordance with NPR 7120.5, NASA Space Flight Program and

Project Management Requirements.

1.4 Zones of Exposure

[PCR 5] The zones of exposure established to define coating system requirements for surfaces located in specific environments shall be determined by the Design Engineer responsible for preparing the coating specification from the following zones:

a. (1) Zone 1a. Surfaces that are directly impinged on by solid rocket booster (SRB) engine exhaust.

(2) Zone 1b. Surfaces that are indirectly impinged on by SRB exhaust.

(3) Zone 1c. Walking surfaces in Zones 1a and 1b.

b. Zone 2. Surfaces that are exposed to elevated temperatures (above 65 °C (above 150 °F)) and/or acid deposition from SRB exhaust with no exhaust impingement.

c. (1) Zone 3a. Surfaces, other than those located in Zones 1 or 2, that are exposed to acid deposition from SRB exhaust products.

(2) Zone 3b. Surfaces that are exposed to other types of chemical contamination (e.g., cooling towers, diesel exhaust stacks, acidic industrial environments, and water treatment facilities).

d. (1) Zone 4a. Surfaces not located in the launch environment but located in a neutral pH corrosive marine industrial environment or other chloride-containing environments.

(2) Zone 4b. Surfaces located in neutral pH exterior environments in any geographical area.

(3) Zone 4c. Surfaces located in indoor environments that are not air-conditioned.

e. (1) Zone 5a. Surfaces located in a continuous indoor air-conditioned environment, such as an office or clean room, where both temperature and humidity are controlled more than 90 percent of the time.

(2) Zone 5b. Surfaces located in a low humidity, high ultraviolet environment, such as a high altitude, arid location.

f. (1) Zone 6a. Surfaces located underground or subject to intermittent or continuous immersion in aqueous environments.

(2) Zone 6b. Surfaces subject to exposure in a chemical/fuel storage environment. Based on the complexity of the liquid stored, this has to be engineered separately in compliance with all federal, state, and local environmental statutory requirements.

g. Zone 7. Surfaces under thermal insulation, such as chilled water, steam, and heated gas lines.

1.5 Method of Specifying Coating Requirements

a. [PCR 6] Specifications referencing this NASA Technical Standard shall include the following:

(1) The type of surface to be coated.

(2) The zone of exposure.

(3) Surface preparation.

(4) Defined paint system.

(5) Coating thicknesses.

(6) The finish color required (when applicable).

These requirements should be assembled in a coating schedule for easy reference.

b. [PCR 7] The coating specification shall contain the following key elements: scope, applicable documents, submittals, environmental protection, waste management, safety/personnel protection, materials, tools and equipment, environmental conditions, work schedule, surface preparation (including a listing of abrasive-sensitive hardware to be prepared or protected), coating schedule, coating mixing and application, quality control inspection, reporting, and final acceptance.

See Appendix D, Coating Specification Key Elements, for a recommended outline of a coating specification and Appendix E for a recommended coating schedule.

1.6 Environmental Stewardship and Health and Safety

a. [PCR 8] Environmental, health, and safety impacts of processes and materials shall be taken into account when employing protective coating methods and techniques.

b. [PCR 9] Alternative, environmentally friendly materials that do not contain hexavalent chromium, lead, cadmium, or hazardous air pollutants (HAPs), such as methyl ethyl ketone, toluene, and xylene, shall be considered when determining the correct coating method/technique for each protective coating application.

c. [PCR 10] Alternative, less hazardous materials shall be considered when determining the correct coating method/technique for each protective coating application to minimize risk in construction, use, and demolition.

d. [PCR 11] Performance criteria defined in this NASA Technical Standard shall take precedent. Coatings containing hazardous materials may be harmful to human health and the environment.

2. APPLICABLE DOCUMENTS

2.1 General

The documents listed in this section contain provisions that constitute requirements of this NASA

Technical Standard as cited in the text.

2.1.1 [PCR 12] The latest issuances of cited documents shall apply unless specific versions are designated.

2.1.2 [PCR 13] Non-use of specifically designated versions shall be approved by the responsible

Technical Authority.

The applicable documents are accessible at http://standards.nasa.gov, may be obtained directly from the Standards Developing Body or other document distributors, or information for obtaining the document is provided.

2.2 Government Documents

Department of Defense (DoD)

MIL-A-22262 Abrasive Blasting Media Ship Hull Blast Cleaning

MIL-PRF-24667 Coating System, Non-skid, for Roll, Spray, or Self-Adhering

Application http://standards.nasa.gov/

QPL 22262

Qualified Products List (Military) of Products Qualified Under

Detail Specification MIL-A-22262 Abrasive Blasting Media Ship

Hull Blast Cleaning

Federal (FED)

29 CFR 1910.134 Respiratory Protection

FED-STD-595 Colors Used in Government Procurement

National Aeronautics and Space Administration (NASA)

NPR 7120.5 NASA Space Flight Program and Project Management

Requirements

KSC-SPEC-F-0006 Heat and Blast Protection Coating Materials and Application

Methods, Specification for

KSC-STD-SF-0004 Ground Piping Systems Color Coding and Identification, Safety

Standard for

NASA-STD-6001

Flammability, Offgassing, and Compatibility Requirements and Test Procedures

(Copies of specifications, standards, drawings, and publications required by suppliers in connection with specific procurement functions should be obtained from the procuring activity or as directed by the Contracting Officer.)

2.3 Non-Government Documents

American Society for Testing and Materials (ASTM)

ASTM A123 Standard Specification for Zinc (Hot-Dip Galvanized) Coatings on

Iron and Steel Products

ASTM A153 Standard Specification for Zinc Coating (Hot-Dip) on Iron and Steel

Hardware

ASTM A653 Standard Specification for Steel Sheet, Zinc-Coated (Galvanized) or

Zinc-Iron Alloy-Coated (Galvannealed) by the Hot-Dip Process

ASTM A780 Standard Practice for Repair of Damaged and Uncoated Areas of Hot-

Dip Galvanized Coatings

ASTM C920 Standard Specification for Elastomeric Joint Sealants

ASTM D520 Standard Specification for Zinc Dust Pigment

ASTM D610 Standard Practice for Evaluating Degree of Rusting on Painted Steel

Surfaces

ASTM D714 Standard Test Method for Evaluating Degree of Blistering of Paints

ASTM D1654 Standard Test Method for Evaluation of Painted or Coated Specimens

Subjected to Corrosive Environments

ASTM D4285 Standard Test Method for Indicating Oil or Water in Compressed Air

ASTM D4417 Standard Test Methods for Field Measurement of Surface Profile of

Blast Cleaned Steel

ASTM D4752 Standard Practice for Measuring MEK Resistance of Ethyl Silicate

(Inorganic) Zinc-Rich Primers by Solvent Rub

NACE International

RP0198 Control of Corrosion Under Thermal Insulation and Fireproofing

Materials – A Systems Approach

RP0288 Inspection of Linings on Steel and Concrete

SP0188 Discontinuity (Holiday) Testing of New Protective Coatings on

Conductive Substrates

National Sanitation Foundation (NSF)

NSF 61 Drinking Water System Components – Health Effects

The Society for Protective Coatings (SSPC)

SSPC-AB 1 Mineral and Slag Abrasives

SSPC-AB 2 Cleanliness of Recycled Ferrous Metallic Abrasives

SSPC-AB 3 Ferrous Metallic Abrasive

SSPC-PA 2 Procedure for Determining Conformance to Dry Coating Thickness

Requirements

SSPC-SP 1 Solvent Cleaning

SSPC-SP 3 Power Tool Cleaning

SSPC-SP 5/

NACE No. 1

White Metal Blast Cleaning

SSPC-SP 10-/

NACE No. 2

Near-White Metal Blast Cleaning

SSPC-SP 11 Power-Tool Cleaning to Bare Metal

SSPC-TU 4 Field Methods for Retrieval and Analysis of Soluble Salts on

Substrates

2.4 Order of Precedence

2.4.1 The requirements and standard practices established in this NASA Technical Standard do not supersede or waive existing requirements and standard practices found in other Agency documentation.

2.4.2 [PCR 14] Conflicts between this NASA Technical Standard and other requirements documents shall be resolved by the responsible Technical Authority.

3. ACRONYMS AND DEFINITIONS

3.1 Acronyms, Abbreviations, and Symbols

° C degree Celsius

° F degree Fahrenheit µg Microgram µm Micrometer

AISC American Institute of Steel Construction

ANSI

APL

American National Standards Institute

Approved Products List

ASME American Society of Mechanical Engineers

ASTM American Society for Testing and Materials

CFR Code of Federal Regulations

CGA Compressed Gas Association

CIP Coating Inspector Program cm Centimeter

DFT dry film thickness

DoD Department of Defense

FED Federal ft Foot

GSE ground support equipment

GU gloss units

HAP hazardous air pollutant hr Hour in Inch

IOT inorganic topcoat kip 1,000 pounds-force km Kilometer kPa Kilopascal

KSC John F. Kennedy Space Center ksi kip per square inch

LLC Limited Liability Company m meter mi mile mil one thousandth of an inch

MIL

mm

Military millimeter

MPa megapascal mph miles per hour

NACE NACE International, formerly known as National Association of

Corrosion Engineers

NASA National Aeronautics and Space Administration

NIOSH National Institute of Occupational Safety and Health

No. number

NSF National Sanitation Foundation

OSHA Occupational Safety and Health Administration oz ounce

PCB polychlorinated biphenyl

PCR Protective Coating Requirement

PDCA Painting and Decorating Contractors of America pH measure of acidity or alkalinity of a solution

PPE personal protective equipment

PPG Pittsburgh Paint and Glass psi pound per square inch

QPL Qualified Products List

RH relative humidity

SB solvent-based

SRB solid rocket booster

SSPC The Society for Protective Coatings

STD standard

TM Technical Manual

TO

TSC

technical order thermal spray coating

VOC volatile organic content

WB water-based

WFT wet film thickness

3.2 Definitions

High-gloss Finish: A minimum of 85 gloss units (GUs) at a 60-degree angle.

Semi-gloss Finish: 60 GU to 85 GU at a 60-degree angle.

4. REQUIREMENTS

4.1 Materials

4.1.1 Abrasive-Blasting Aggregate

a. [PCR 15] Blasting aggregates shall be approved materials in accordance with MIL-A-

22262, Abrasive Blasting Media Ship Hull Blast Cleaning; or SSPC-AB 1, Mineral and Slag

Abrasives, Type I or II, Class A; or steel grit in accordance with SSPC-AB 3, Ferrous Metallic

Abrasive, Class 1.

b. [PCR 16] Only materials approved in Qualified Products List (QPL) 22262, Qualified

Products List: List of Products Qualified Under Military Specification MIL-A-22262, shall be used.

c. [PCR 17] The abrasive grade selected shall produce the required surface profile and possess physical properties that are compatible with the requirements of this NASA Technical

Standard.

d. [PCR 18] The new steel grit shall be a neutral pH (6.0 to 8.0), rust-free and oil-free, dry, commercial-grade blasting grit with a hardness of 40 to 50 Rockwell C.

e. [PCR 19] Recycled steel grit shall be in accordance with SSPC-AB 2, Cleanliness of

Recycled Ferrous Metallic Abrasives.

f. [PCR 20] The size shall be selected to produce the required anchor profile.

For paint removal or cleaning of aluminum, stainless steel, and fiberglass, plastic media in accordance with MIL-P-85891, Plastic Media for Removal of Organic Coatings, may be used as an alternate.

g. [PCR 21] Only aggregates that are free of crystalline silica shall be selected for use at

NASA unless exemptions to this policy are coordinated with the local Occupational Health

Office.

h. [PCR 22] Blasting aggregate for abrasion-sensitive hardware (such as bellows, gimbal joints, and other thin-walled components) shall be materials that do not change the surface profile.

(1) [PCR 23] Blasting operations shall not produce holes, cause distortion, remove metal, or cause thinning of the substrate.

4.1.2 Protective Coatings, Thinners, and Cleaners

The following paragraphs establish minimum requirements for each generic type of protective coating specified in this NASA Technical Standard. See section 4.4.3.1 for coating intercoat compatibility requirements.

a. [PCR 24] All coatings shall possess physical properties and handling characteristics that are compatible with the application requirements of this NASA Technical Standard.

b. [PCR 25] All coatings shall be self-curing.

c. [PCR 26] Thinners and cleaners for each coating shall be procured from the manufacturer of the coating.

d. [PCR 27] Procurement awards for coatings to be supplied according to this NASA

Technical Standard shall be made only for those products in the Approved Products List (APL).

e. [PCR 28] Application characteristics shall be judged acceptable prior to beach exposure testing.

f. [PCR 29] Protective coatings shall be compatible with fluids expected in the areas to the extent required to prevent fire, explosion, or damage to facility, hardware, and GSE.

g. [PCR 30] All coating materials, when used in areas where exposure to hypergolic propellants could occur, shall be compatible with the propellants in accordance with NASA-

STD-6001, Flammability, Offgassing, and Compatibility Requirements and Test Procedures.

Interested parties should be aware of this requirement and are urged to arrange for testing of their product so that they may be eligible for award of contracts or orders for coatings to be supplied in accordance with this NASA Technical Standard. To arrange for product testing and the testing criteria, manufacturers must contact the Engineering Directorate, NASA, John F.

Kennedy Space (KSC) Center, FL 32899 or contact the Corrosion Technology Laboratory at http://corrosion.ksc.nasa.gov.

4.1.2.1 Inorganic Zinc Coatings

Inorganic zinc coatings that have been approved are listed in Appendix A, Approved Products

List for Inorganic Zinc Coatings.

http://corrosion.ksc.nasa.gov/

a. [PCR 31] To be listed, a coating shall meet the following minimum requirements:

(1) Self-curing, multiple-component.

(2) Dry-temperature resistance to 400 °C (750 °F) for 24 hours.

(3) Minimum shelf life of 6 months when stored in accordance with manufacturer’s instructions.

(4) Minimum of 83 percent zinc by weight in the applied dry film.

(5) Contain Type III zinc dust pigment in accordance with ASTM D520, Standard

Specification for Zinc Dust Pigment, and be asbestos-free, polychlorinated biphenyl (PCB)-free, lead-free, cadmium-free, and chromate-free (less than 0.002 percent by weight of mixed coating).

(6) Attain a rating of not less than 9 in accordance with ASTM D610, Standard

Practice for Evaluating Degree of Rusting on Painted Steel Surfaces; and ASTM

D1654, Standard Test Method for Evaluation of Painted or Coated Specimens

Subjected to Corrosive Environments, when applied to composite carbon steel test panels and exposed at the KSC Beach Corrosion Test Site for the following periods:

A. 18 months for initial acceptance.

B. 5 years for final acceptance.

b. [PCR 32] Application characteristics shall be judged acceptable prior to beach testing.

4.1.2.2 Primer and/or Intermediate Coatings

These coatings are listed in Appendix B, Approved Products List for Topcoat Systems.

4.1.2.2.1 Inhibitive Polyamide Epoxy Coatings

[PCR 33] Polyamide epoxy coatings shall conform to the following minimum requirements:

a. Polyamide-cured.

b. Rust-inhibitive.

c. PCB-free, lead-free, cadmium-free, and chromate-free (less than 0.002 percent by weight of mixed coating).

d. Suitable as a primer for carbon steel, galvanized steel, and aluminum.

e. Suitable as an intermediate coat between an inorganic zinc primer and an aliphatic polyurethane finish coat.

f. Meet the compatibility requirements of section 4.4.3.1.

g. Contain a minimum of 40 percent solids by volume.

4.1.2.2.2 Noninhibitive Polyamide Epoxy Coatings

[PCR 34] Polyamide epoxy coatings shall conform to the following minimum requirements:

a. Polyamide-cured.

b. PCB-free, lead-free, cadmium-free, and chromate-free (less than 0.002 percent by

c. Suitable as an intermediate coat between inorganic zinc primer and an aliphatic polyurethane finish coat.

d. Meet the compatibility requirements of section 4.4.3.1.

e. Contain a minimum of 40 percent solids by volume.

f. Not to be used as a primer on carbon steel.

4.1.2.2.3 Water-Reducible Intermediate Coatings

[PCR 35] Water-reducible intermediate coatings shall conform to the following minimum requirements:

a. Self-curing, one or two packages, water reducible.

c. Suitable as an intermediate coat between inorganic zinc primers and water-reducible topcoats.

d. Meet the compatibility requirements of section 4.4.3.1.

e. Contain a minimum of 30 percent solids by volume.

f. Not to be used as a primer on steel.

4.1.2.3 Finish Coatings

4.1.2.3.1 Aliphatic Polyurethane Coatings

[PCR 36] Aliphatic polyurethane coatings shall conform to the following minimum requirements:

a. Catalyst isocyanate cured.

b. High-gloss finish (minimum 85 gloss units (GUs) at a 60-degree angle).

c. Retain gloss and color upon prolonged exterior exposure.

d. Suitable as an exterior finish coat over an inorganic zinc primer with a polyamide epoxy intermediate coat.

e. Meet the compatibility requirements of section 4.4.3.1.

f. Contain a minimum of 44 percent solids by volume.

g. PCB-free, lead-free, cadmium-free, and chromate-free (less than 0.002 percent by

h. Attain a numerical rating of not less than 8 in accordance with ASTM D610 and

ASTM D1654 and a numerical rating of not less than 9F in accordance with ASTM D714, Standard Test Method for Evaluating Degree of Blistering of Paints, when applied as a system to composite carbon steel test panels and exposed at the KSC Beach Corrosion Test Site for the following periods:

(1) 18 months for initial acceptance.

(2) 5 years for final acceptance.

4.1.2.3.2 Water-Reducible Topcoats

[PCR 37] Water-reducible topcoats shall conform to the following minimum requirements:

a. Self-curing, one or two packages, water-reducible.

c. Retain gloss and color upon prolonged exterior exposure.

d. Semi-gloss or high-gloss finish. (Semi-gloss is defined as 60 GU to 85 GU at a 60-degree angle; high gloss is defined as a minimum 85 GU at a 60-degree angle.)

e. Meet the compatibility requirements of section 4.4.3.1.

f. Attain a numerical rating of not less than 8 in accordance with ASTM D610 and

ASTM D1654 and a numerical rating of not less than 9F in accordance with ASTM D714, when applied as a system to composite carbon steel test panels and exposed at the KSC Beach

Corrosion Test Site for the following periods:

4.1.2.3.3 Inorganic Topcoats (IOTs)

[PCR 38] IOTs shall conform to the following minimum requirements:

a. Dry-temperature resistance to 400 °C (750 °F) for 24 hours.

b. Suitable as a topcoat for inorganic zinc and galvanized steel in high-temperature environments.

c. Listed as an approved coating system (see Appendix B).

d. PCB-free, lead-free, cadmium-free, and chromate-free (less than 0.002 percent by

e. Attain a rating of not less than 9 in accordance with ASTM D610 and ASTM D1654 when applied to composite carbon steel test panels and exposed at the KSC Beach Corrosion

Test Site for the following periods:

4.1.2.3.4 Polysiloxane Topcoats

[PCR 39] Polysiloxane topcoats shall conform to the following minimum requirements:

a. Suitable as a finish coat for exterior exposure.

b. Contain a minimum of 44 percent solids by volume.

c. High-gloss finish (minimum 85 GU at a 60-degree angle).

d. Retain gloss and color on prolonged outdoor exposure.

e. PCB-free, lead-free, cadmium-free, and chromate-free (less than 0.002 percent by

f. Listed as an approved coating system (see Appendix B).

g. Attain a numerical rating of not less than 8 in accordance with ASTM D610 and

ASTM D1654 and a numerical rating of not less than 9F in accordance with ASTM D714 when applied as a system to composite carbon steel test panels and exposed at the KSC Beach

Corrosion Test Site for the following periods:

4.1.2.4 Epoxy Mastic Coatings

[PCR 40] Epoxy mastic coatings shall conform to the following minimum requirements:

a. Specifically intended for use over mechanically cleaned steel.

b. Contain a minimum of 80 percent solids by volume.

c. Two-component, catalyst-cured, aluminum-pigmented.

d. PCB-free, lead-free, cadmium-free, and chromate-free (less than 0.002 percent by

Examples of epoxy mastic coating that currently meet these requirements include:

(1) Ameron Amerlock 400 AL.

(2) Devoe Bar Rust 239.

(3) PPG Pittguard DTR.

(4) Sherwin-Williams Epolon Mastic.

4.1.2.5 Coal Tar Epoxy

a. [PCR 41] Coal tar epoxy coating shall be a two-component, high-build epoxy of low volatile organic content (VOC).

b. [PCR 42] The coal tar epoxy shall contain, at a minimum, 65 percent solids by volume.

c. [PCR 43] The coal tar epoxy shall produce a one-coat thickness of 405 µm to 510 µm

(16 mil to 20 mil) per coat dry film thickness (DFT).

Examples of coal tar epoxies that currently meet these requirements include the following:

a. Sherwin-Williams Hi-Mil Sher-Tar.

b. Made Well 1103.

c. Devoe Devtar 247.

4.1.2.6 Potable Water Epoxy

[PCR 44] All coatings for potable water immersion service shall be three-coat epoxy systems that are certified by NSF Standard 61, Drinking Water System Components – Health Effects.

Some NSF-approved products include:

a. Ameron Amercoat 395.

b. Devoe Bar Rust 233.

c. Sherwin-Williams Potable Water Epoxy.

4.1.2.7 Nonskid Coating

[PCR 45] Approved nonskid coatings shall conform to MIL-PRF-24667, Coating System, Non-skid, for Roll, Spray, or Self-Adhering Application, Type 1, Composition G, as supplied by

American Safety Technologies, Inc., 565 Eagle Rock Avenue, Roseland, NJ 07068, telephone

(800) 631-7841 (< www.astantislip.com >), or an approved equivalent (Primer MS 7C, Topcoat

MS 400G, Color Topping MS-200).

4.1.3 Sealants/Caulking

a. [PCR 46] Sealants shall be self-curing, single-component, polysulfide rubber or polyurethane material only, conforming to ASTM C920, Standard Specification for Elastomeric

Joint Sealants, Type S, Grade NS, Class 25, use NT, A, and O.

b. [PCR 47] If not topcoated, the caulking shall match the color of the joint surface being caulked.

c. [PCR 48] If caulking is to be used in a clean-room environment, an approved material with low offgassing characteristics in accordance with NASA-STD-6001 shall be selected.

4.1.4 Chip-Free Clean-Room Paint

[PCR 49] Paint systems for metal substrates in clean-rooms may be required to pass tests for adhesion, offgassing, flammability, vacuum outgassing, and hypergolic compatibility.

Offgassing, flammability, and hypergolic compatibility testing shall be in accordance with

NASA-STD-6001, Supplemental Test Procedure A.7.

4.2 Equipment

4.2.1 Compressed Air

a. [PCR 50] The compressed air system shall be capable of delivering a continuous nozzle pressure to achieve the required surface cleanliness and profile, typically 620 kPa (90 psi) minimum to each blast nozzle in operation.

The required air capacity depends upon the configuration of the abrasive system used. The air system should comply with the instructions and recommendations of the manufacturer of the abrasive-blasting system.

b. [PCR 51] The compressed air system shall be equipped with oil and moisture separators to ensure only clean, dry air is provided to the service outlet.

c. [PCR 52] The compressed air system shall comply with Occupational Safety and

Health Administration (OSHA), American National Standards Institute (ANSI), and National

Institute of Occupational Safety and Health (NIOSH) configurations.

d. [PCR 53] Air distribution manifolds shall conform to American Society of

Mechanical Engineers (ASME) standards.

4.2.2 Abrasive-Blasting System

a. [PCR 54] The abrasive-blasting system shall comply with OSHA, ANSI, and NIOSH configurations consisting of, but not limited to, the following:

(1) A remote-controlled welded pressure pot conforming to ASME standards.

(2) The required length of blast hose.

(3) A venturi nozzle.

(4) A respiratory air-line filter.

(5) A blast hood approved by the Mine Safety and Health Administration/NIOSH with the required length of air hose.

b. [PCR 55] The blasting system shall be designed to produce the specified cleanliness level and profile when coupled with the available compressed air supply.

4.2.3 Coating Application System

[PCR 56] The coating application equipment shall be an airless spray system, conventional spray system, or other approved equipment in accordance with the coating manufacturer's recommendations and section 4.4.3.6.

4.2.4 Respiratory Protection

[PCR 57] Respiratory protection shall be in accordance with 29 CFR 1910.134, Respiratory

Protection, and Center respiratory protection requirements.

4.3 Safety and Health Requirements

a. [PCR 58] Necessary precautions, in accordance with OSHA regulations, manufacturers’ recommendations, and industry standards, shall be taken to ensure the safety and health of personnel performing the work required by this NASA Technical Standard and personnel who may be affected by such work.

Some of the materials handled in accordance with this document are combustible, or toxic, or both.

b. [PCR 59] The Contractor shall provide equipment as required for safe and healthful application and instruction to the users regarding the hazards and proper handling and disposal procedures to prevent injury or illness.

c. [PCR 60] The Contractor shall provide safe access to all areas for the coating inspector.

d. [PCR 61] The Contractor shall submit a written safety and health plan that includes a

Hazard Communication Program, a Respiratory Protection Program, and a Hearing Conservation

Program that conforms to OSHA requirements and industry standards.

e. [PCR 62] Where the contractor is required to remove surface coatings that contain

PCB, lead, chromium, mercury, or cadmium, or other regulated materials, the Contractor shall include specific provisions in the safety and health plan for complying with all Federal, State, Local, and NASA Center-specific requirements.

4.3.1 Environmental Requirements

The operations described in this NASA Technical Standard have the potential to impact the environment.

a. [PCR 63] All local, state, and federal environmental regulations, as well as the NASA

Center’s environmental policies, shall be followed.

b. [PCR 64] Questions regarding these regulations and policies shall be directed to the local environmental management organization.

4.3.2 Personal Protective Equipment (PPE)

a. [PCR 65] When engineering controls cannot be implemented to protect workers, then

PPE and/or administrative controls shall be used.

b. [PCR 66] Where required, PPE shall be used in accordance with all federal, state, NASA, and Center requirements.

c. [PCR 67] Both the supervisors and the workers shall be properly instructed, trained, and certified in the selection, use, and maintenance of PPE.

4.4 General Requirements

4.4.1 Applicator Qualifications

a. [PCR 68] To ensure the highest quality of workmanship, only coating applicators who have worked in the painting trade sufficiently long enough to master the use of all applicable tools and materials shall be assigned to perform the work described herein.

The applicator's proficiency and ability to attain the required quality of workmanship for the specified coating system can be verified by testing and qualification in accordance with ASTM

D4228, Standard Practice for Qualification of Coating Applicators for Application of Coatings to Steel Surfaces.

b. [PCR 69] In addition, the coating applicators shall provide written evidence of having successfully completed a comprehensive training program, such as Painting and Decorating

Contractors of America (PDCA)/NACE/SSPC Industrial Painters Training, or equivalent.

c. [PCR 70] The Contractor shall provide all painting personnel an orientation on the proper mixing and application of the coatings specified, particularly inorganic zinc coatings.

d. [PCR 71] Topics in the orientation of proper mixing and application of the specified coatings (particularly for inorganic zinc coatings) shall include specification requirements, material application characteristics, and inspection criteria.

e. [PCR 72] The mixing or application of coatings shall be performed only by personnel who have received training.

f. [PCR 73] The Contractor shall prepare representative sample areas that meet specification requirements.

4.4.2 Preparation of Surfaces

a. [PCR 74] All surfaces to be coated shall be clean, dry, and free from oil, grease, dirt, dust, corrosion, peeling paint, caulking, weld spatter, and any other surface contaminants.

b. [PCR 75] All surfaces that cannot be accessed after fabrication, erection, or installation shall be prepared and coated while accessible.

c. [PCR 76] Surface preparation and coating operations shall be sequenced, so that freshly applied coatings will not be contaminated by dust or foreign matter.

d. [PCR 77] All equipment and adjacent surfaces not to be coated shall be protected from surface preparation operations.

e. [PCR 78] Working mechanisms shall be protected against intrusion of the abrasive.

f. [PCR 79] All surfaces shall be degreased, as required, before subsequent surface preparation procedures or the application of protective coatings, or both.

g. [PCR 80] The following sections provide the surface preparation techniques that shall be used when specified in section 4.5.

4.4.2.1 Cleaning and Degreasing

a. [PCR 81] Degreasing shall be by solvent cleaning, detergent washing, or steam cleaning in accordance with SSPC-SP 1, Solvent Cleaning.

b. [PCR 82] This degreasing procedure shall be followed when cleaning carbon steel, galvanized steel, stainless steel, or aluminum.

c. [PCR 83] Selection of solvents shall be in accordance with use requirements and applicable federal, state, and NASA environmental policies.

d. [PCR 84] Chlorofluorocarbon solvents shall not be used.

e. [PCR 85] Water washing, using clean potable water, shall be done when high levels of chloride (>5 µg/cm2) or other undesirable contaminants are found on the surfaces.

f. [PCR 86] Water washing shall be accomplished using standard industrial pressure cleaners with a pressure-versus-volume output balance that will ensure thorough and productive cleaning.

g. [PCR 87] All water washing or pressure cleaning operations shall comply with all

Federal, State, Local, and NASA Center environmental requirements.

h. [PCR 88] The cleaned surface shall be free of loose coatings, chlorides, dirt, dust, mildew, grinding/welding/cutting debris, and visible contaminants.

i. [PCR 89] The surface shall be clean and dry prior to the abrasive-blasting operations and application of coatings.

4.4.2.2 Abrasive Blasting

a. [PCR 90] The abrasive-blasting aggregate shall be clean and dry and conform to section

4.1.1.

b. [PCR 91] The abrasive-blasting system shall conform to section 4.2.2.

c. [PCR 92] Abrasive blasting shall be in accordance with the applicable paragraphs in section 4.5.

d. [PCR 93] Abrasive residues shall be removed from the surface, leaving it clean and dry before the coatings are applied.

e. [PCR 94] All particulate emissions generated during abrasive-blasting operations shall be contained.

f. [PCR 95] The containment system shall be designed to comply with all applicable federal, state, and local regulations as well as all NASA policies.

g. [PCR 96] Exemptions to the requirement in 4.4.2.2f shall be coordinated with the local environmental management office.

h. [PCR 97] The aggregate used to prepare abrasive-sensitive hardware such as bellows, gimbal joints, and other thin-walled components shall be carefully identified and selected.

4.4.2.3 Mechanical Cleaning Methods

[PCR 98] Mechanical methods shall be in accordance with the applicable paragraph in section

4.5.

4.4.3 Application of Coatings

a. [PCR 99] All prepared surfaces shall be coated within 6 hours after surface preparation and before corrosion or recontamination occurs. As an exception, surfaces prepared under temperature and humidity control may be coated after 6 hours but only after inspection of the surface preparation confirms that the cleanliness level has met the specified standards.

b. [PCR 100] Any surface that shows corrosion or contamination, regardless of the length of time after preparation, shall be prepared again.

c. [PCR 101] Because the application and handling characteristics of all coatings will vary, adequate written instructions from the manufacturer are essential and shall be closely followed in conjunction with the requirements defined herein to obtain optimum performance.

d. [PCR 102] The manufacturer’s written recommendations for thinning, mixing, handling, and applying the product shall be strictly followed.

e. [PCR 103] All coatings shall be thoroughly worked into all joints, crevices, and open spaces.

f. [PCR 104] All newly coated surfaces shall be protected from damage.

g. [PCR 105] All equipment and adjacent surfaces not to be coated shall be protected from overspray and splattered coatings.

h. [PCR106] Particulate emissions shall be contained during all spray-painting operations.

i. [PCR 107] The containment system shall be designed to comply with all federal, state, and local regulations as well as all NASA policies.

j. [PCR 108] Exemptions to this requirement shall be coordinated with the local environmental management organization.

4.4.3.1 Coating Systems

a. [PCR 109] Coating systems for specified uses and substrates shall be as defined in section 4.5 and conform to section 4.1.2.

b. [PCR 110] All thinners and cleaners shall be products of the coating manufacturer, except as defined in section 4.1.2.7.

c. [PCR 111] To ensure intercoat compatibility, coating systems consisting of more than one coat shall be products of the same manufacturer.

d. [PCR 112] Continuity of the coating manufacturer’s system shall be maintained for the duration of an individual project.

4.4.3.2 Colors

a. [PCR 113] Inorganic zinc coatings shall be pigmented so that there is a definite contrast between the coating and the dull gray appearance of the blasted steel surface during the coating application.

b. [PCR 114] Color coding for fluid system piping shall be in accordance with KSC-STD-

SF-0004, Ground Piping Systems Color Coding and Identification, Safety Standard for.

c. [PCR 115] Finish coat colors shall be in accordance with the following FED-STD-

595, Colors Used in Government Procurement, color numbers using pigments free of PCB, lead, chromium, and cadmium:

(1) White, No. 17925.

(2) Blue, No. 15102 (safety).

(3) Yellow, No. 13538 (standard).

(4) Yellow, No. 13655 (safety).

(5) Red, No. 11136.

(6) Red, No. 11105 (safety).

(7) Black, No. 17038.

(8) Green, No. 14110 (safety).

(9) Gray, No. 16187 (safety).

(10) Brown, No. 10080 (safety).

(11) Gray, No. 16473 (standard).

4.4.3.3 Storage of Coating Materials

a. [PCR 116] Coating materials and thinners shall be stored in their original containers with the manufacturer’s name, product identification, shelf life, and batch number.

b. [PCR 117] Coating materials, thinners, and cleaners shall be stored in tightly closed containers in a covered, well-ventilated area where they will not be exposed to sparks, flame, direct sunlight, extreme heat, or rainfall.

c. [PCR 118] The manufacturer’s written instructions for storage limitations shall be followed.

d. [PCR 119] Tarpaulins shall not be used as the sole means of covering coating materials for storage.

e. [PCR 120] Material Safety Data Sheets for coating materials and thinners shall be maintained or made accessible to users in the area.

f. [PCR 121] The Contractor shall submit a written plan for approval for storage of coating materials for coordination with the local safety/fire/environmental organization.

4.4.3.4 Mixing and Application Instructions

a. [PCR 122] Coating materials shall be thoroughly mixed prior to application with a mechanical mixing instrument that will not induce air into the coating, such as a Jiffy Mixer, manufactured by the Jiffy Mixer Company (< www.jiffymixer.com >), Inc., Riverside, CA, or an approved equivalent.

b. [PCR 123] The mixer shall be powered by an air motor or an explosion-proof electric motor.

c. [PCR 124] All mixing operations shall be performed over an impervious surface with provisions to prevent runoff to grade of any spilled material.

d. [PCR 125] The mixed coating material shall be strained through a 30-mesh to 60-mesh screen prior to application.

e. [PCR 126] Thinning shall be for viscosity control only.

f. [PCR 127] If thinner is required, the amount recommended by the manufacturer of the thinner shall be used.

g. [PCR 128] The material shall be agitated as required during application to maintain a uniform suspension of solids.

h. [PCR 129] Continuous rapid agitation shall be avoided.

i. [PCR 130] Spray equipment shall be adjusted to produce an even, wet coat with minimum overspray.

j. [PCR 131] The conventional pressure pot, when used, shall be kept at approximately the same level or above the spray gun, so that the material is delivered properly.

k. [PCR 132] Coatings shall be applied in even, parallel passes, overlapping 50 percent.

4.4.3.5 Weather Conditions

a. [PCR 133] No coating shall be applied when contamination from any source (i.e., rainfall) is imminent…