Steel Material for Fabrication of Miter Gate Anchorages
Closed Solicitation Posted
This opportunity was awarded. See the award notice from .
- Solicitation number
- W912ES25QA039
- Agency
-
ENDIST St Paul
US Army Corps of Engineers, Department of Defense
- Responses due
- Set-aside
- No set-aside
Opportunity facts
- NAICS code
- 331110 Iron and Steel Mills and Ferroalloy Manufacturing
- PSC
- 9515 Plate, Sheet, Strip, Foil, And Leaf
- Place of performance
- Pleasant Valley, Iowa 52767, United States
Notice details come from SAM.gov. Updated .
About this opportunity
The U.S. Army Corps of Engineers, St. Paul District is procuring three ASTM A709 HPS 70WF steel plates for fabricating miter gate anchorage components at Locks 5, 6, and 9 along the upper Mississippi River. Each steel plate must be 4 inches thick by 8 feet by 20 feet and cut into three equal pieces measuring 80 inches by 96 inches. The steel must comply with stringent technical specifications including DFARS 252.225-7030 restrictions, Buy American Act requirements, specific tensile and hardness testing standards per ASTM A709 Table 1, and impact testing requirements for fracture control applications. Contractors must submit verifiable mill certifications electronically in PDF format prior to shipment, with the material requiring proper marking, clean surfaces free of contaminants, and appropriate bundling for forklift or crane handling. The solicitation was posted on July 14, 2025, with responses due by July 28, 2025, and delivery required no later than October 20, 2025.
This procurement does not utilize any set-aside designations and is classified under NAICS code 331110 for Iron and Steel Mills and Ferroalloy Manufacturing. No incumbent contractors or award values are specified in the solicitation documents. The contract requires delivery of three specially cut steel plates totaling nine individual pieces when divided, with delivery scheduled within approximately three months of the response deadline. All materials must be delivered to the US Army Corps of Engineers MRPO-Service Base located at 25549 182nd Street in Pleasant Valley, Iowa, during business hours of 7:00 AM to 3:00 PM, Monday through Thursday, excluding federal holidays. Contractors must provide 24-hour advance notice and request escorted entry to the facility, with the steel intended for critical infrastructure maintenance on the upper Mississippi River lock system.
Notice text
2 versions
Update #2 · Latest ·
SCOPE OF WORK
Steel Material for
Fabrication of Miter Gate Anchorages
U.S. Army Corps of Engineers, St. Paul District
1. General Description.
The Contractor shall provide three (3) ASTM A709 HPS 70WF 4" thick x 8' x 20' steel plates cut into three (3) equal pieces (80" x 96") and include delivery to US Army Corps of Engineers Service Base in Pleasant Valley, IA. The intended use is for the fabrication of miter gate anchorage components for Locks 5, 6 and 9 along the upper Mississippi River. Delivery MUST be no later than October 20, 2025.
2. ASTM A 709 HPS 70WF Plate Specifications. (See ASTM Attachment A 709-24)
A. Steel must be compliant with DF ARS 252.225-7030, Restriction on Acquisition of Carbon, Alloy, and Armor Steel Plate.
B. Dimensions of master plate is 4" thick x 8' x20' and then cut into three equal sections of 4" x 6' 8" x 8' (plus/minus 1/2"). See
attached drawing.
C. A 4" x 4" sample of steel to be cut from each piece (see attached pdf for acceptable coupon locations) is acceptable to conduct testing.
D. Tensile and hardness testing must meet minimums described in ASTM A 709 Table 1 for HPS70W
E. The plate is a tension component of a member that requires fracture control practice. Impact test the plate in accordance with A673/A673M. Results must meet the requirements of ASTM A709 Table 12 for Zone 3 for HPS 70WF.
F. Chemical Requirements must conform to ASTM A709 Table 7 for HPS 70W.
G. Must conform to Buy American Act.
H. Final product shall be clean and free of any oil or grease, dross, slag or burrs. All cut edges (regardless of method) shall have a
surface roughness acceptable for welding.
I. Final product shall be legibly marked with the applicable designation, grade, heat number, size and thickness, name brand, or
trademark of the manufacturer for identification and shipment.
J. Bundle and band the steel material as required for shipping, with cribbing at minimum six inches above the base of the shipping
platform to allow offloading with a forklift and/or crane. Covering of the material during shipment is not required.
K. Mill Certificates shall be submitted after the Contractor verifies the material meets all the aforementioned test requirements.
3. Submittals
The Contractor shall submit a verifiable mill certification electronically in pdf format via email to both the Government Contracting Officer's representative and the Government technical point of contact prior to shipment of the material. The mill certificate must match the tag on the material.
The Government technical point of contact is:
Available at award.
4. Delivery Schedule
Delivery of the ASTM A709 HPS 70WF shall be no later than October 20th, 2025. Soonest possible delivery is requested if possible.
All material shall be delivered to the following address during business hours of07:00am to 03:00pm, Monday through Thursday, excluding federal holidays. Please give the POC listed below 24 hours advance notice and request ESCORTED entry to the facility.
US Army Corps of Engineers
MRPO-Service Base
25549, 182nd St.
Pleasant Valley, IA, 52767
POC: Available at award.
Update #1 ·
SCOPE OF WORK
Steel Material for
Fabrication of Miter Gate Anchorages
U.S. Army Corps of Engineers, St. Paul District
1. General Description.
The Contractor shall provide three (3) ASTM A709 HPS 70WF 4" thick x 8' x 20' steel plates cut into three (3) equal pieces (80" x 96") and include delivery to US Army Corps of Engineers Service Base in Pleasant Valley, IA. The intended use is for the fabrication of miter gate anchorage components for Locks 5, 6 and 9 along the upper Mississippi River. Delivery MUST be no later than October 20, 2025.
2. ASTM A 709 HPS 70WF Plate Specifications. (See ASTM Attachment A 709-24)
A. Steel must be compliant with DF ARS 252.225-7030, Restriction on Acquisition of Carbon, Alloy, and Armor Steel Plate.
B. Dimensions of master plate is 4" thick x 8' x20' and then cut into three equal sections of 4" x 6' 8" x 8' (plus/minus 1/2"). See
attached drawing.
C. A 4" x 4" sample of steel to be cut from any of the four comers of each piece is acceptable to conduct testing.
D. Tensile and hardness testing must meet minimums described in ASTM A 709 Table 1 for HPS70W
E. The plate is a tension component of a member that requires fracture control practice. Impact test the plate in accordance with A673/A673M. Results must meet the requirements of ASTM A709 Table 12 for Zone 3 for HPS 70WF.
F. Chemical Requirements must conform to ASTM A709 Table 7 for HPS 70W.
G. Must conform to Buy American Act.
H. Final product shall be clean and free of any oil or grease, dross, slag or burrs. All cut edges (regardless of method) shall have a
surface roughness acceptable for welding.
I. Final product shall be legibly marked with the applicable designation, grade, heat number, size and thickness, name brand, or
trademark of the manufacturer for identification and shipment.
J. Bundle and band the steel material as required for shipping, with cribbing at minimum six inches above the base of the shipping
platform to allow offloading with a forklift and/or crane. Covering of the material during shipment is not required.
K. Mill Certificates shall be submitted after the Contractor verifies the material meets all the aforementioned test requirements.
3. Submittals
The Contractor shall submit a verifiable mill certification electronically in pdf format via email to both the Government Contracting Officer's representative and the Government technical point of contact prior to shipment of the material. The mill certificate must match the tag on the material.
The Government technical point of contact is:
Available at award.
4. Delivery Schedule
Delivery of the ASTM A709 HPS 70WF shall be no later than October 20th, 2025. Soonest possible delivery is requested if possible.
All material shall be delivered to the following address during business hours of07:00am to 03:00pm, Monday through Thursday, excluding federal holidays. Please give the POC listed below 24 hours advance notice and request ESCORTED entry to the facility.
US Army Corps of Engineers
MRPO-Service Base
25549, 182nd St.
Pleasant Valley, IA, 52767
POC: Available at award.
Files
Notice history
| Notice | Type | Posted |
|---|---|---|
| Steel Material for Fabrication of Miter Gate Anchorages | Award Notice | |
| This notice | Solicitation |
Similar open opportunities
| Opportunity | Agency | Set-aside | Responses due |
|---|---|---|---|
| Steel plates | — | Total Small Business | |
| Request for Information for On-Site Fabrication and Assembly of a Three-Bay High-Performance Magazine (HPM) Structure | Engineer Research and Development Center | No set-aside | |
| Debris Boom Supply and Install at Harry S. Truman Lake Project | ENDIST Kansas City | No set-aside | |
| PLATE, METAL, METRIC and BEAM, H-SHAPE, METRIC for Ship Repair Facility and Japan Regional Maintenance Center (SRF-JRMC), US Naval Base, Yokosuka, Japan. | Naval Supply Systems Command | No set-aside | |
| Purchase of 2 or 3 Temporary Road Bridges | Forest Service | No set-aside |
On GovTribe
Work this opportunity
- Track it in your pipeline
- Find teaming partners
- Similar opportunities
- Ask GovTribe AI about this opportunity