This document contains a purchase description for 34 MAGNA-F antenna bases. Key details include specifications for base materials, laminate curing processes, fairing inspection standards, filler material sanding requirements, and resin mixture ratios and curing times for various finishing processes. The related federal contract opportunity is a pre-solicitation notice from the Department of the Army National Guard seeking MAGNA-F antenna bases, with a solicitation number provided but no further information on response dates, award timing, or other procurement details.

View the file

On GovTribe

Work with this file

  • Download the original file
  • Contacts named in this file
  • Similar government files
  • Ask GovTribe AI about this file
Try for free Login

Text version

The file's text, extracted by GovTribe without its formatting.

CLIN 0001) MAGNA-F Antenna Bases – 34ea a.) Base, Antenna Support b.) Pre-Preg Layup and Cure IAW Park Electrochemical, process spec E765 PS1000 and Ply Table c.) Filler materials shall be wet sanded with clean 20 grit abrasive paper.

d.) Curing of laminate and again after all machining operations are completed, visually inspect fairing IAW ASTM D2563 acceptance Level III e.) All undimensioned feathers shall have a profile tolerance of .060 as applicable.

f.) Prepare FN 6 using Part A and Part B mixture ratio of 100:24 by weight and cure at ambient temp for 24hr. POT life is 90 min @ 72deg F.

g.) Prepare FN 7 using part A and Part B mixture ration of 100:2 by weight. Tack free (MINUTES AFTER GELATION) 10 min. Finishing schedule (MINUTES AFTER GELATION) 15-25 min. POT LIFE is 5-6 min @ 77°F.

h.) Prepare FN 7 (ALTN) using part A and part B mixture ration of 100:50 by weight./ Cure for 24hr at greater than 77deg F. After 5hrs @ 77deg F, the compound may be sanded and painted. POT LIFE is 30min @ 77deg F.