350_Paint_Kitchen_Attachment_D.pdf

T E C H N I C A L B U L L E T I N

6937 WEST MILL ROAD MILWAUKEE, WI 53218-1225 TELEPHONE 414-353-4200 FAX 414-353-0286 EMAIL coatings@hentzen.com

The information contained here is to our knowledge true and accurate but all suggestions are made without guarantee since conditions of use are beyond our control. Nothing contained herein shall be construed as a recommendation to use any product in conflict with existing patents covering any material or use.

22167WEP/22170CEH

Two Component Off-White High Solids Epoxy Primer per MIL-DTL-53022E, Type IV

PRODUCT DESCRIPTION

EPOXZEN is the trade name for Hentzen's Epoxy Coatings. This two component primer meets the requirements of MIL-DTL-53022E.

HANDLING & STORAGE

The containers should be stored away from direct sunlight and heat.

Freezing is not harmful if reheated gently to room temperature prior to use.

PHYSICAL CHARACTERISTICS

22167WEP Off-White Epoxy Primer - Component A:

Weight per Gallon: 11.98 lbs. .30

Weight Solids: 71.55 1.00%

Volume Solids: 53.26 1.00%

Viscosity: 63 - 75 KU's

22170CEH Epoxy Hardener - Component B:

Weight per Gallon: 8.01 lbs. .25

Weight Solids: 39.29 1.00%

Volume Solids: 33.67 1.00%

Admixed Characteristics:

Catalyzation Ratio: 4:1 by volume

Weight per Gallon: 11.18 lbs. .30

Weight Solids: 66.93 1.00%

Volume Solids: 49.35 1.00%

VOC: 2.80 maximum

Viscosity: 20 - 32" @ #3 Zahn

Theoretical Coverage - sq. ft./gl.

@ 1.0 mil dry film thickness: 791.5

Useable Pot Life: Approximately 4 - 6 hours to 1½ times initial viscosity.

To extend the pot life, regulations permitting, some additional thinner may be required to reduce the viscosity. A fresh mixture of Component A and B could also be added to lower the pot viscosity.

Shelf Life: 18 months from date of mfg. when stored between

40ºF and 80ºF, in a cool dry area out of direct sunlight.

Gloss @ 60o Meter: 10 - 45 @ 1.5 mil DFT

Cure Schedule - Air Dry @ 77oF

& 50% Relative Humidity:

Set to Touch: 10 - 20 minutes

Dry Hard: 1 - 1½ hours

Dry Through: 4 hours

Recoat: 2 - 24 hours

Full Resistance Properties: 7 days

Force Cure Recommendation: 20 - 30 minutes @ 180oF

ENVIRONMENTAL REPORT

Volatile Content (Wt.%): 33.07

Organic Volatile Content (Wt.%): 19.93

Density of Organic Volatile (Wt./Gl.): 7.02

Density of Solid Content (Wt./Gl.): 15.16

Exempt Solvent Content (Wt.%): 12.98

Exempt Solvent Content (Vol.%): 18.90

VOC Minus Water: 2.80 maximum

DIRECTIONS FOR USE

Component A should be thoroughly agitated prior to blending. After agitating Component A, mix 4 volumes of Component A to 1 volume of

Component B and mix the two Components well. Allow the admixed product 30 minutes to induct prior to spraying. No further reduction is necessary. Mix only what you will use in 6 hours. After that time, the product will have gained viscosity and will eventually gel. If further reduction is needed use a VOC exempt solvent such as Methyl Acetate, Tertiary Butyl Acetate or Acetone.

PRECAUTIONS & SAFETY

Do not apply at temperatures below 50oF.

Read all container labels.

Read Material Safety Data Sheet.

Keep away from open flame and sparks.

CLEAN-UP

Clean equipment immediately after use with 00212SST-1 Solvent Blend or equivalent.

August 24, 2016