COMPOUND,

OVERMOLD MATERIAL

DWG NO. REVSH

DISTRIBUTION STATEMENT C. DISTRIBUTION AUTHORIZED TO U.S. GOVERNMENT AGENCIES AND THEIR CONTRACTORS.

CRITICAL TECHNOLOGY, 14 FEB 2008. OTHER REQUESTS FOR THIS DOCUMENT SHALL BE REFERRED TO UNITED STATES

MARINE CORPS, LOGISTICS COMMAND (P732), ALBANY, GA.

WARNING - THIS DOCUMENT CONTAINS TECHNICAL DATA WHOSE EXPORT IS RESTRICTED BY THE ARMS EXPORT

CONTROL ACT (TITLE 22, U.S.C., SEC 2751. ET SEQ.) OR THE EXPORT ADMINISTRATION ACT OF 1979, AS AMENDED, TITLE

50, U.S.C., APP. 2401 ET SEQ. VIOLATIONS OF THESE EXPORT LAWS ARE SUBJECT TO SEVERE CRIMINAL PENALTIES.

DISSEMINATE IN ACCORDANCE WITH PROVISIONS OF DOD DIRECTIVE 5230.25.

CAD MAINTAINED. CHANGES SHALL BE

INCORPORATED BY THE DESIGN ACTIVITY.

CAD VERSION: AUTOCAD 2011

SUGGESTED SOURCE OF SUPPLY

CAGE SOURCE VENDOR PART NUMBER CONTROL NUMBER

05238 LUBRIZOL ADVANCED MATERIALS, INC.

9911 BRECKSVILLE RD

CLEVELAND, OH 44141-3247

TELE: 800-380-5397

ESTANE 58211 08002B0163

VENDOR ITEM CONTROL DRAWING

LOG

THIRD ANGLE PROJECTION

INTERPRETATION OF

DRAWING, DIM AND TOL PER

ASME Y14.100 AND ASME Y14.5M

UNLESS OTHERWISE SPECIFIED

DIMENSIONS ARE IN INCHES

TOL ON ANGLE ± 1°

2 PL ± .03 AND 3 PL ± .010

NOTES - UNLESS OTHERWISE SPECIFIED:

1. IDENTIFICATION OF THE SUGGESTED SOURCE OF SUPPLY HEREON IS NOT TO BE

CONSTRUED AS A GUARANTEE OF PRESENT OR CONTINUED AVAILABILITY AS A SOURCE

OF SUPPLY FOR THE ITEM(S).

2. THIS DEVICE SHALL COMPLY WITH THE FOLLOWING SPECIFICATIONS:

A. CONFIGURATION:

- MATERIAL TYPE: 90A POLYETHER-TYPE THERMOPLASTIC POLYURETHANE (TPU).

- FEATURES: HALOGENATED FLAME RETARDANT COMPOUND - HIGH HARDNESS

- PRIMARY USE: EXTRUSION - WIRE AND CABLE JACKETING

B. PRIMARY USE:

- EXTRUSION - WIRE AND CABLE JACKETING.

C. PACKAGING:

- SUPPLIED IN PELLET FORM AND PACKAGED IN 50 LB BAGS OR 1000 LB BOXES.

D. PREPARATION:

- PRIOR TO PROCESSING, DRY AT 104 DEGREES CELCIUS FOR 2 TO 4 HOURS.

- DRY MATERIAL IN A DESICCANT TYPE DRYER. TARGET DEW POINT IS 40 DEGREES CELCIUS.

- MAXIMUM MOISTURE LEVEL SHOULD BE 0.02 PERCENT.

E. PROCESSING:

- TPU CAN BE PROCESSED ON ANY CONVENTIONAL EXTRUDER.

- PROCESS IN ACCORDANCE WITH MANUFACTURERS RECOMMENDED INSTRUCTIONS.

F. PROPERTIES:

* PRIOR TO TESTING, SAMPLES SHALL BE CONDITIONED AT 23 DEGREES C FOR 48 HOURS.

* PROPERTIES BASED ON EXTRUDED SHEET (30 MILS).

* LISTED VALUES ARE TYPICAL (AVERAGE) VALUES.

REINALDO ZOZAYA

TONY HALTER

COREY DICKERSON

20100415

20100415

20100415

20100415

APPROVED FOR THE COMMAND

H. JEFFERSON WOOD

PROPERTY VALUE UNIT TEST METHOD

HARDNESS (5 SEC) 90 + / - 3 SHORE A ASTM D-2240

SPECIFIC GRAVITY 1.29 ASTM D-792

TENSILE STRENGTH 4050 (27.9) PSI (MPa) ASTM D-412

ULTIMATE ELONGATION 340 % ASTM D-412

TENSILE STRESS AT:

- 100 % ELONGATION 1250 (8.6) PSI (MPa) ASTM D-412

- 300 % ELONGATION 2150 (14.8) PSI (MPa) ASTM D-412

TEAR STRENGTH

- GRAVES 480 (8.6) LB/IN (KG/MM) ASTM D-624 (DIE C)

- TROUSER

125 (2.2) LB/IN (KG/MM) ASTM D-470

TABER LOSS (1000 REV) .0083 (235) OZ (MG) ASTM D-3389 (H18, 1000G)

TG (BY DSC) -36 (-38) DEGREES F (C) LUBRIZON ADVANCED MATERIALS

APPLICATION

USED ONNEXT ASSY

AN/UYK-128(V)

07006B0031

PART

DASH NO.

NA

07006B0042

07006B0044

07006B0046

07006B0047

07006B0048

- HJWBASELINE RELEASE 20120405

07006B0021

07006B0045

07006B0023

03002B7641

7011050

7011048

7011047

7011046

7011044

7011043

7011042

7011032

7011031

7011024

7011022

08002B0042

7011051

07006B0022

CAPT THOMAS A. SIKORA

5 APRIL 2012

07006B0019

07006B0020

07006B0025

07006B0026

07006B0027

07006B0028

07006B0032

07006B0033

07006B0040

07006B0043

07006B0062

07006B0146

10017B0030

10017B0041