INS75_101_2_Insitu_ES2_TDS_print.pdf
PDF 41 KB Posted
- Attached to
- WAPA VC REPLACE 9 TON PCU AND SPLIT UNIT Federal contract opportunity
- Solicitation number
- 140P8221Q0036
View the file
Other files for this federal contract opportunity
| File | Type | Posted |
|---|---|---|
| Mechanical_Drawings_(Sheet_M-3)_.pdf | ||
| Existing_Unit_Location.pdf | ||
| Sol_140P8221Q0036.pdf | ||
| WAPA-VC_Floor_Plan-Work_Locations.pdf | ||
| WAPA-TStellNewmanVC100_Elec.pdf | ||
| MBH_Conversion_to_Ton.pdf | ||
| Existing_Unit_Product_Tag.pdf | ||
| SCA_Wage_Determination.pdf |
On GovTribe
Work with this file on GovTribe
- Download the original file
- Contacts named in this file
- Similar government files
- Ask GovTribe AI about this file
Text version
TECHNICAL DATA SHEET
Insitu® Spray Coat ES2
Spray-Applied, Anti-Corrosion Coil and Cabinet Coating
PRODUCT DESCRIPTION
Insitu® Spray Coat ES2 is a water-based and water-reducible synthetic flexible polymer anti-corrosion coating specifically designed for the protection of HVAC&R coils and components. Insitu® Spray Coat ES2 is formulated with (embedded stainless steel) pigments to improve adhesion, moisture resistance UV protection and corrosion durability. The product is applied at our facilities or on-site at your premises after HVAC&R units have been manufactured.
SPECIFICATIONS
Heat exchanger (HX) coils, cabinets and optional internal HVAC components shall have a water-based synthetic polymer coating with ES2 pigment spray-applied with no material bridging between fins. The spray coating process will ensure a uniform dry film thickness of 15-30 μm (0.6-1.2 mils) and meet 5B rating crosshatch adhesion per ASTM D3359. Corrosion durability will be confirmed through testing to no less than 10,000 hours salt spray resistance per C5-I and DIN 53167 (ASTM B117) using aluminum test coupons.
APPLICATIONS IDEALLY SUITED FOR INSITU® SPRAY COAT
• Heat exchanger coils (water, condenser, evaporator, DX)
• Mini-splits
• Packaged Rooftops
• Condensing Units
• Modular Air-handlers
• Air-cooled Chillers
• Interior & exterior HVAC cabinetry and copper piping
GENERAL DESCRIPTION
– SUBJECT TO CHANGES OR DEVIATIONS
TECHNICAL PROPERTIES
RESISTANCE TO:
CORROSION RESISTANCE
ES2 pigments are made from a high-performance stainless alloy and resistant to corrosive conditions. ES2 pigments are therefore suitable for even the most corrosive environments and will maintain their appearance after many years exposure. ES2 pigments help to reduce the effect of thermal loss / degradation by enhancing heat transfer thru the coating. Typical transfer loss is ≤ 1%.
UV DEGRADATION
ES2 pigments form a multi-layer structure throughout the paint film. This creates a barrier layer which reflects sunlight away from the paint film preventing ultraviolet rays from penetrating. As a result, UV degradation of individual polymer molecules is eliminated, the film integrity is maintained, and the pigment particles are well anchored to the substrate.
The resultant smooth, hard finish stops dirt from accumulating.
MOISTURE
The multi-layer structure of the ES2 pigments slows the passage of water molecules into the film and acts as an effective moisture barrier.
This prevents subsequent swelling and deterioration of the protective film.
ModineCoatings.comCopyright © 2019 Modine
PROPERTY TEST METHOD PERFORMANCE
Salt Spray DIN 53167/ASTM B117 Exceeds 10,000 hours
Water Immersion ASTM D870 500 hours minimum
Pencil Hardness ASTM D3363 HB-F
Cross Hatch Adhesion ASTM D3359 5B
Humidity ASTM D2247 500 hours minimum
UV Resistance ASTM D4587 500 hours minimum
Mandrel Bend (Flexibility) ASTM D522M Pass
Mold Resistance ASTM G21 Pass
C5-I Continuous Condensation ISO 6270 Pass
C5-I Salt Spray ISO 7523 Pass
C5-I Chemical Resistance ISO 2812-1 Pass
INS75-101.2