P1. JML 31890850 Attachment 2.pdf

ATTACHMENT 1: Material Order (Doc #31890850)

Note: Requirements listed herein does not relieve the prime vendor’s responsibility of meeting all the requirements of T9074-BD-GIB-

010/0300 (Rev 2)

ITEM DESCRIPTION

LOCAL STOCK NUMBER: N/A

DESCRIPTION: PLATE, STEEL ALLOY GRADE HY-100, TYPE II, IN ACCORDANCE WITH NAVSEA

TECH PUB T9074-BD-GIB-010/0300 REV 2

THICKNESS: 1.62”

CUT SIZE: 5’ X 20’ Plate. Plate may be cut into 3ea, 5’ x 6’-8” sections for ease of shipping. Each piece requires material markings per para B.3.11 of Appendix B of T9074-BD-GIB-010/0300 (REV2).

Vendor shall adhere to paragraph (2) of this document.

QUANTITY: 100 SQ FT (1 PM)

ACQUISITION REQUIREMENTS:

A. “BASE MATERIALS FOR CRITICAL APPLICATIONS: REQUIREMENTS FOR LOW ALLOY

STEEL PLATE, FORGINGS, CASTINGS, SHAPES, BARS, AND HEADS OF HY-80/100/130

AND HSLA-80/100, NAVSEA TECHNICAL PUBLICATION T9074-BD-GIB-010/0300 rev 2, DTD

18 DEC 2012.

B. Grade HY-100.

C. Latest in effect at time of award.

D. Required.

E. Not required.

F. N/A.

G. IAW Paragraph 4.5.2.

H. ASTM-D3951-18

ADDITIONAL ACQUISITION REQUIREMENTS PER PARAGRAPH 6.2 OF APPENDIX B OF

T9074-BD-GIB-010/0300 (REV2) :

(A) “BASE MATERIALS FOR CRITICAL APPLICATIONS: REQUIREMENTS FOR LOW ALLOY

STEEL PLATE, FORGINGS, CASTINGS, SHAPES, BARS, AND HEADS OF HY-80/100/130

AND HSLA-80/100, T9074-BD-GIB-010/0300 rev 2, DTD 18 DEC 2012.

(B) 1 PM, 1.62” thick 5’ x 20’. Plate may be cut into 3, 5’ x 6’-8” sections for ease of shipping.

Vendor shall adhere to paragraph (2) of “Additional Requirements”.

(C) Type II, Grade HY-100.

(D) Virgin raw material is not required.

(E) Ultimate tensile strength to be provided for information only, IAW Appendix B, Table B-2.

(F) Simulated stress relief sample is not required.

(G) Weld repair is prohibited prior to heat treatment. Weld repair of mill defects after heat treatment shall be in accordance with paragraph B.3.6.1

(H) No alternate ultrasonic acceptance standard is specified.

(I) Ultrasonic testing for internal soundness and thickness is required, see paragraph B.3.7

(J) N/A for Type II plating.

(K) NAVSEA T9074-BD-GIB-010/0300 Rev 2.

(L) Thickness of plate is 1.62”. Plate to be furnished by thickness with thickness tolerance as specified in Table B-6 (0.062”)

(M) Flatness tolerances shall be within the limits specified, Table B-9.

(N) Required.

(O) Any coating that complies with Appendix K is acceptable.

(P) Explosion testing per paragraph B.3.12 (First Article Testing Only).

(Q) First Article specimens shall be located in areas shown on Figure B-1.

(R) N/A. HY-100 plate procurement only.

(S) N/A. HY-100 procurement only.

Additional Requirements:

1) The vendor shall provide a statement, in their Certificate of Conformance, that they have maintained procedures demonstrated in first article testing and include the revision of the process control plan used and the date of the most recent first article approval.

2) If the vendor cuts the plate into 3 pieces IAW para (B) of this document, then for each plate, the vendor shall indentation stamp each plate permanently IAW para B.3.11. This includes, but not limited to the final rolling direction of the plate with respect to the hot top of the ingot or the leading edge of the slab. The vendor shall also mark the plates such that PHNSY can reconstruct the original plate, as it was prior to cutting.

3) If the vendor does not cut the plate into 3 pieces, the original plate shall still be indentation stamped permanently IAW para B.3.11 of T9074-BD-GIB-010/0300 REV 2. This includes, but not limited to the final rolling direction of the plate with respect to the hot top of the ingot or the leading edge of the slab.

4) Vendor shall specify, on the Certificate of Conformance, whether the direction of rolling stamped on the plate IAW (2) is parallel or perpendicular to the longitudinal axis of the ingot.

5) Vendor shall ensure that all hand written data provided to PHNSY is legible and readable for certification purposes.